SARV COAT 6729

alkyd PHENOLIC TOPCOAT



Description

Sarv coat 6729 is a one component alkyd finish coat modified with phenolic.

 

Physical Data

 

Finish............................................... Flat

Colour............................................. Upon request

Volume Solids............................... 60±2%

Specific Gravity............................ 1.30±0.05 gr/cm3

Flash Point..................................... 23°C

Recommended D.F.T................... 50-60 microns

Theoretical coverage.................... 12-10 m²/lit.

                                                          8-6 m²/kg

Practical Coverage....................... Depends on loss factor

Touch dry....................................... 1 hrs at 25°C

Fully cured..................................... 4 days at 25°C

Shelf life ........................................ 24 months at 20°C

Thermal Resistance...................... Continuous 120°C

                                                      Non-continuous 130°C

Package.......................................... 20 liter container

 

Application Details

Application method..................... Air /Airless spray, Brush, Roller

Application temperature............. 10-50°c

Mixing ratio................................... single pack

Thinner/Cleaner............................ SVT- 67

Recoat interval.............................. Min. 24 hrs.

                                                           Max 72 hrs

Outstanding Characteristics

  • Excellent oil resistance.
  • Excellent chemical resistance against acids alkalis.
  • Excellent adhesion
  • Excellent weather resistance.
  • Excellent Hardness
  • Fast air drying.

Recommended Use

As a protection coating in industrial and marine structures over concrete or metal surface.

Resistance to a variety of chemicals , fuel oils and solvents.

As a general purpose is suitable for lining storage tanks ship tanks exposed to immersion, splash sea mater

Surface Preparation

The surface must be clean and dry . All dirt, grease, mill scales and any other foreign materials should be removed.

Old primed surfaces must be smoothly wire brushed.

Blast to sa 3 ISO 8501 or SSPC 5,the roughness profile should be 40-75 micron.