SARV COAT 1761pure silicone COATINGS |
|
DescriptionSarv coat 1761 is a high temperature resistant, aluminum pigmented primer, based on silicone resin.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. Aluminum Volume Solids............................... 32±2% Specific Gravity............................ 1.05 ±0.05 gr/Cm3 Flash Point..................................... 25°C Recommended D.F.T................... 25-40 microns Theoretical Coverage................... 12.8-8 sqm/lit 12.19-7.62 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... after thermal curing Thermal Resistance...................... Continuous 600°C Noncotinuous 650 °C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 125 bar/1800 Psi Mixing............................................. Single pack Thinner/Cleaner............................ SVT-17 Pot life ............................................ N/A Recoat interval min:.................... 24 hrs at 20 °C Recoat interval max:................... (see Remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose primer, for use in protection of steel surfaces subjected to temperatures up to 600°C. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, SSPC-10. |
SARV COAT 1861acrylic silicone COATINGS |
|
|
|
|
|
DescriptionSarv coat 1861 is a high Temperature resistant, paint, based on modified silicone-acrylic resin.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. aluminium Volume Solids............................... 38±2% Specific Gravity............................ 1.05±0.05 gr/Cm3 Flash Point..................................... 25°C Recommended D.F.T................... 25-40 microns Theoretical Coverage................... 15.2-9.5 sqm/lit 14.47-9.04 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 120 min at 20°C Hard dry......................................... after thermal curing Thermal Resistance...................... Continuous 400°C noncontinuous 440 °C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 125 bar/1800 Psi Mixing ratio................................... Single pack Thinner/Cleaner............................ SVT-18 Pot life ............................................ N/A Recoat interval min:.................... 24 hrs at 20 °C Recoat interval max:................... (see Remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a temperature resistant paint, for use in protection of steel surfaces subjected to temperatures up to 400°C. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Abrasive blasting to Sa2½, SSPC-10. |
SARV COAT 1862acrylics silicone COATINGS |
|
|
|
|
|
DescriptionSarv coat 1862 is a temperature resistant, paint, based on modified silicone-acrylic resin.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. Aluminum Volume Solids............................... 38±2% Specific Gravity............................ 1±0.05 gr/m3 Flash Point..................................... 25°C Recommended D.F.T................... 25-40 microns Theoretical Coverage................... 15.2-9.5 sqm/lit 15.2-9.5 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hours at 20°C Hard dry......................................... after thermal curing Thermal Resistance...................... Continuous 250°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 125 bar/1800 Psi Mixing ratio................................... Single pack Thinner/Cleaner............................ SVT-18 Pot life ............................................ N/A Recoat interval min:.................... 24 hrs at 20 °C Recoat interval max:................... (see Remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a temperature resistance paint, for use in protection of steel surfaces subjected to temperatures up to 250°C. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Abrasive blasting to Sa ½, SSPC-10. |
SARV COAT 1862-7coloured acrylic silicone COATINGS |
|
|
|
|
|
DescriptionSarv coat 1862-7 is a temperature resistant, paint, based on modified silicone-acrylic resin.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. limited Volume Solids............................... 41±2% Specific Gravity............................ 1.05±0.05 gr/cm3 Flash Point..................................... 25°C Recommended D.F.T................... 25-40 microns Theoretical Coverage................... 16.4-10.2 sqm/lit 15.6-9.7 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hours at 20°C Hard dry......................................... after thermal curing Thermal Resistance...................... Continuous 250°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 125 bar/1800 Psi Mixing ratio................................... Single pack Thinner/Cleaner............................ SVT-18 Pot life ............................................ N/A Recoat interval min:.................... 24 hrs at 20 °C Recoat interval max:................... (see Remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a temperature resistant paint, for use in protection of steel surfaces subjected to temperatures up to 250°C. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Abrasive blasting to Sa2½, SSPC-10. |
SARV COAT 1862-8coloured acrylic silicone COATINGS |
|
|
|
|
|
DescriptionSarv coat 1862-8 is a temperature resistant, paint, based on modified silicone-acrylic resin.
|
Physical Data
Finish............................................... Semi flat-Semi Gloss Colour............................................. limited Red, Black-Grey, Orange Volume Solids............................... 41±2% Specific Gravity............................ 1.05±0.05 gr/m3 Flash Point..................................... 25°C Recommended D.F.T................... 25-40 microns Theoretical Coverage................... 16.4-10.2 sqm/lit 15.6-9.7 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hours at 20°C Hard dry......................................... after thermal curing Thermal Resistance...................... Continuous 200°C Shelf life......................................... 1 year at 25°C Packageing..................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 125 bar/1800 Psi Mixing ratio................................... Single pack Thinner/Cleaner............................ SVT-18 Pot life ............................................ N/A Recoat interval min:.................... 24 hrs at 20 °C Recoat interval max:................... (see Remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a temperature resistant paint, for use in protection of steel surfaces subjected to temperatures up to 200°C. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, SSPC-10. |
SARV COAT 19833 pack inorcanic zinc silicate COATINGS |
|
|
|
|
|
DescriptionSarv coat 1983 is a 3-pack, self curing(reacting with atmospheric moisture), solvent based zinc ethyl silicate coating.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 61±2% Specific Gravity............................ 2.70 ±0.05 gr/m3 Flash Point..................................... 14°C Zinc content in dry film............... 90±1% Recommended D.F.T................... 50-75 microns Theoretical coverage.................... 12.2-8.13 sqm/lit 4.43-2.95 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 10 min Hard dry......................................... 24 hrs at relative Humidity up 65-75 % Thermal Resistance...................... continuous 400°C Non-continuous 420°C Shelf life Liquids.......................... 3(part A), 12(part B) months at 20°C Powder Indefinite
Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 100 bar/1500 Psi Application temperature............. 10 to 40°C Mixing ratio................................... A/B/C 5/3/25 by weight Thinner/Cleaner............................ SVT-19 Pot life ............................................ 4 hrs at 20°C Recoat interval min...................... (see remarks overleaf) Recoat interval max.................... none(see remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose, heavy duty rust preventing primer suitable for long term protection of steel structures exposed to severely corrosive and abrasive environment . |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, SSPC-10 with a sharp-edged surface profile corresponding to rugotest No. 3, BN10a, Keane-Tator comparator, 2.0 G/S or ISO comparator medium.(G) |
SARV COAT 1983-72 Pack inorcanic zinc silicate COATINGS |
|
|
|
|
|
DescriptionSarv coat 1983-7 is a 2-pack, self curing (reacting with atmospheric moisture), solvent based zinc ethyl silicate coating.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 61±2% Specific Gravity............................ 2.70 ±0.05 gr/m3 Flash Point..................................... 14°C Recommended D.F.T................... 50-75 microns Theoretical coverage.................... 12.2-8.13 sqm/lit 4.43-2.95 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 10 min Hard dry......................................... 1 days at relative humidity up 65-75 % Thermal Resistance...................... continuous 400°C Non-continuous 420°C Shelf life Liquids.......................... 3 months at 20°C Powder ........................... Indefinite
Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 100 bar/1500 Psi Application temperature............. 10 to 40°C Mixing ratio................................... A/B 8/25 by weight Thinner/Cleaner............................ SVT-19 Pot life ............................................ 4 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a general purpose, heavy duty rust preventing primer suitable for long term protection of steel structures exposed to severely corrosive and abrasive environment . |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, SSPC-10 with a sharp-edged surface profile corresponding to rugotest No. 3, BN9a, Keane-Tator comparator, 2.0 G/S or ISO comparator medium.(G) |
|
SARV COAT 1983-8 |
2 pack inorcanic zinc silicate shopprimer COATINGS |
|
|
|
|
|
DescriptionSarv coat 1983-8 is a three-pack, medium zinc, self curing (reacting with atmospheric moisture), and solvent borne zinc ethyl silicate & weldabel coating.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 42±2% Specific Gravity............................ 1.65 ±0.1 gr/m3 Flash Point..................................... 10°C Recommended D.F.T................... 20-25 microns Theoretical coverage.................... 21-16.8 sqm/lit 12.7-10.1 sqm/kg Touch dry....................................... 2 hrs Hard dry......................................... 1 days at relative Humidity up 65-75 % Shelf life Liquids.......................... 3 months Powder Indefinite Package.......................................... 5/3/4 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Application temperature............. 5 to 40°C Mixing ratio................................... 1/3/4 by weight Thinner/Cleaner............................ SVT-19 Pot life ............................................ 8 hrs Recoat interval.............................. Min(see remarks overleaf) Max none(see remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a temperature protective primer for the coating of steel work prior to the fabrication & for relatively long term protection of blast cleaned steel plates & other structural steel. |
|
Surface PreparationRemove oil & grease, etc. with suitable detergent Grit blasting to minimum Sa 2½ with a surface profile equivalent to Ragotest No.3, BN10a. |
|
SARV COAT 1983-9 |
2 pakc silico silicate primer |
|
|
|
|
|
DescriptionSarv coat 1983-9 is a 2-pack, self curing modified ethyl silicate primer. Specially formulated for cold galvanizing of welds & seams.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 60±1% Specific Gravity............................ 2.70 ±0.5 gr/m3 Flash Point..................................... 10°C Recommended D.F.T................... 40-75 microns Theoretical coverage.................... 15-8 sqm/lit 5.5-2.96 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 10 min Hard dry......................................... 1 days at relative Humidity up to 50 % Thermal Resistance...................... continuous 400°C Non-continuous 420 °C Shelf life Liquids.......................... 3 months at 25 °C Powder Indefinite Package.......................................... 24 & 8 kg container Application DetailsApplication method .................... Air/Airless spray, Brush Application temperature............. 10 to 40°C Mixing ratio................................... 1 A /3 B Thinner/Cleaner............................ SVT-19 Pot life ............................................ 4 hrs Over coat interval......................... Min.24 hrs(full cured) Max. 3 months
|
Outstanding Characteristics
|
|
Recommended UseAs a general purpose, leavy duty rust preventing primer, suitable for long term protection of steel structures exposed to severely corrosive and abrasive environment. |
|
Surface PreparationRemove oil & grease, etc. with suitable detergent Grit blasting to minimum Sa 2 ½ with a surface profile equivalent to Ragotest No.3, BN10a. |
|
SARV COAT 2729 |
vinyl sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2729 is a physically drying sealer based on a vinyl copolymer resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Non-pigmented Volume Solids............................... 36±2% Specific Gravity............................ 0.95 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 20-40 microns Theoretical coverage.................... 18-9 sqm/lit ......................................................... 18.9-9.5 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 20 hrs at 20°C Hard dry......................................... 16 hrs at 20 °C Shelf life......................................... 1 year Package.......................................... 4 or 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 4 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a sealer coat on metal and concrete surfaces and as intermediate coat on zinc silicates to minimize popping. |
|
Surface PreparationFor previously primed surfaces with sarv coat 1983 the surface must be clean and dry. All dirt grease, mill- scales and any other foreign materials should be removed. |
|
SARV COAT 2730 |
vinyl anti-fouling COATINGS |
|
|
|
|
|
DescriptionSarv coat 2730 is a physically drying anti-fouling topcoat based on a vinyl copolymer resin with a high toxicity level.
|
Physical Data
Finish............................................... Flat Colour............................................. Red Volume Solids............................... 52±2% Specific Gravity............................ 1.6 ±0.1 gr/cm3 Flash Point..................................... 30°C Recommended D.F.T................... 30-50 microns Theoretical coverage.................... 17.3-10.4 sqm/lit 10.8-6.5 sqm/kg Touch dry....................................... 30 min at 20°C Hard dry......................................... 180 min at 35 °C Shelf life......................................... 1 year Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a anti-fouling topcoat for vinyl system on exterior of immersed marine steel structures and ships. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, mill scale, salt and loose paint. Old painted surfaces must be cleaned with high pressure water guns. |
|
SARV COAT 2731 |
vinyl top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 2731 is a physically drying topcoat based on a vinyl copolymer resin.
|
Physical Data
Finish............................................... Gloss, semi gloss Colour............................................. Upon request Volume Solids............................... 30±2% Specific Gravity............................ 1.20 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 30-50 microns Theoretical coverage.................... 10-6 sqm/lit 8.33-5 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 days at 20 °C Thermal Resistance...................... 80°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a versatile top coat for vinyl systems on exterior steel structures exposed in moderately to severely industrial and marine corrosive environment. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, mill scale, salt and loose paint. |
|
SARV COAT 2732 |
vinyl intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 2732 is a physically drying topcoat based on a vinyl copolymer resin.
|
Physical Data
Finish............................................... Flat Colour............................................. upon request Volume Solids............................... 33±2% Specific Gravity............................ 1.35 ±0.05 gr/cm3 Flash Point..................................... 23°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 8.25-5.5 sqm/lit 6.11-4.07 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 days at 20 °C Thermal Resistance...................... 80°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 months |
Outstanding Characteristics
|
|
Recommended UseAs a versatile topcoat for vinyl systems on exterior steel structures exposed in moderately to severely industrial and marine corrosive environment. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, mill scale, salt and loose paint. |
|
SARV COAT 2733 |
vinyl zinc chromate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2733 is a physically drying general primer based on a vinyl copolymer resin pigmented with zinc chromate as corrosion preventing pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Yellow Volume Solids............................... 32±2% Specific Gravity............................ 1.27 ±0.05 gr/cm3 Flash Point..................................... 23°C Dry film thickness......................... 40-60 microns Theoretical coverage.................... 8-5.3 sqm/lit 6.3-4.2 sqm/kg Touch dry....................................... 2 hrs at 40°C Dry to handle................................. 1 days at 20 °C Thermal Resistance...................... 80°C Practical Coverage....................... depends on loss factor Shelf life......................................... 1 year at 25°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a primer for vinly systems on exterior of marine steel structures, or as an intermediate coat on epoxy primer. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (For repair and maintenance) Abrasive blasting to Sa 2½, SSPC-10 (for new steel) |
|
SARV COAT 2734 |
vinyl red lead primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2734 is a physically drying general primer based on a vinyl copolymer resin pigmented with red lead oxide as corrosion preventing pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Orange Volume Solids............................... 30±2% Specific Gravity............................ 1.53 ±0.05 gr/m3 Flash Point..................................... 23°C Dry Film Thickness....................... 40-60 microns Theoretical coverage.................... 7.5-5 sqm/lit 5-3.26 sqm/kg Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 days at 20 °C Thermal Resistance...................... 80°C Practical Coverage....................... depends on loss factor Shelf life......................................... 1 year at 25°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a primer for vinyl systems on exterior of marine of marine steel structures, or as an intermediate coat on epoxy primer. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (For repair and maintenance) Abrasive blasting to Sa 2½, SSPC-10 (for new steel) |
|
SARV COAT 2735 |
vinyl red oxie primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2735 is a general purpose vinyl red oxide primer based on vinyl copolymer resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Red-Brown Volume Solids............................... 32±2% Specific Gravity............................ 1.33 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 8-5.33 sqm/lit 6.4 sqm/lit Practical Coverage....................... depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 days at 20 °C Shelf life......................................... 1 year at 25°C Thermal Resistance...................... continuous 80°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 - 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs versatile primer for vinyl system on steel structures exposed in moderately to severly industrial & marine corrosive environments. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (For repair and maintenance) Abrasive blasting to Sa 2½, SSPC-10 (for new steel) |
|
SARV COAT 2736 |
vinyl primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2736 is a physically drying general primer based on a vinyl copolymer resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Yellow, other shades may be availabe Volume Solids............................... 34±2% Specific Gravity............................ 1.30 ±0.05 gr/m3 Flash Point..................................... 23°C Dry film thickness......................... 30-50 microns Theoretical coverage.................... 11.33-6.8 sqm/lit 8.71-5.23 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 days at 20 °C Thermal Resistance...................... 80°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .019"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 to 40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-27 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 2 moths |
Outstanding Characteristics
|
|
Recommended UseAs a primer for vinyl systems on exterior steel structures, or as an intermediate coat on sarv coat 1983 to minimize popping. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2½ (For repair and maintenance) Abrasive blasting to Sa 2½, SSPC-10 (for new steel) |
|
SARV COAT 2885 |
vinyl etch primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 2885 is a two component etch primer based on polyvinyl butyral.
|
Physical Data
Finish............................................... Flat Colour............................................. Dark Yellow Volume Solids............................... 12±2% Specific Gravity............................ 0.88 ±0.93 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 7-13 microns Theoretical coverage.................... 28-14 sqm/lit 29.47-14.73 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 10 min at 20°C Dry to handle................................. 30 min at 20 °C Shelf life......................................... 1 year at 25 °C Package.......................................... 4 & 16 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller Application temperature............. 10 - 50°C Mixing ratio................................... Base/Hardener 4/ 1 by weight Thinner/Cleaner............................ SVT-28 Pot life ............................................ 5 hours Recoat interval.............................. Min 6 hrs Max 24 moths |
Outstanding Characteristics
|
|
Recommended UseAs a preconstruction primer and suitable for nonferrous surfaces such as galvanized steel and aluminium, to improve performance of subsequent coats. |
|
Surface PreparationThe surface must be clean, and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed. |
|
SARV COAT 2968 |
vinyl decorative COATINGS |
|
|
|
|
|
DescriptionSarv coat 2968 is a versatile water base decorative paint based on PVA.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 35±2% Specific Gravity............................ 1.4 ±0.05 gr/m3 Recommended D.F.T................... 75 microns Theoretical coverage.................... 4.6 sqm/lit 3.3 sqm/kg Touch dry....................................... 1-2 hrs at 20°C Hard dry......................................... 2-3 dary at 20 °C Practical Coverage....................... Depends on loss factor Shelf life......................................... 1 year Package.......................................... 4 liter container Application DetailsApplication method .................... Air spray, Brush, Roller Application temperature............. 10 - 50°C Mixing ratio................................... single pack Thinner/Cleaner............................ water Pot life ............................................ N/A Recoat interval.............................. Min 5 hrs Max none |
Outstanding Characteristics
|
|
Recommended UseAs a decorative coat on building walls and massonaries. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, salt and loose paint. |
|
SARV COAT 3168 |
ACRYLIC Traffic COATINGS |
|
|
|
|
|
DescriptionSarv coat 3168 is a quick drying based on thermoplastic acrylic resin.
|
Physical Data
Finish............................................... Flat Colour............................................. white, yellow, black Volume Solids............................... 49±2% Specific Gravity............................ 1.37±0.05 gr/cm3 Flash point..................................... 33 °C Recommended D.F.T................... 200-400 microns Theoretical coverage.................... 2.4-1.2 sqm/lit. 1.7-0.85 sqm/kg Practical Coverage....................... Depends on loss factor Dry through.................................... 30 min Shelf life ........................................ 12 months Package.......................................... 20 liter container Application DetailsApplication method..................... Automatic spray or hand application Application temperature............. 0-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-31 Pot life ............................................ N/A Recoat interval.............................. No limitation
|
Outstanding Characteristics
|
|
Recommended UseSuitable for use on concrete and asphalt, specially for road marking. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as dust, grease, oil, salt and loose paint.
|
|
SARV COAT 3568 |
ACRYLIC baking enamel COATINGS |
|
|
|
|
|
DescriptionSarv coat 3568 is baking glossy topcoat based on thermoset acrylic resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. Upon rquest Volume Solids............................... 36±3% Specific Gravity............................ 1.15±0.1gr/cm3 Depends on coloul Flash Point..................................... 23°c Dry film thickness......................... 25-40 microns Theoretical coverage.................... 14.4-9 sqm/lit. 12.5-7.8 sqm/kg Practical Coverage....................... Depends on loss factor Flashing time................................. 10 min Stoving conditions........................ 15-20 min at 150-170°c Shelflife ......................................... 12 months at 25°c Package.......................................... 20 liter container Application DetailsApplication method..................... Air/Brush, Roller, deep Nozzle oridice................................ 021” Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-35 Pot life ............................................ N/A Recoat interval.............................. wet on wet or after partially curing |
Outstanding Characteristics
|
|
Recommended UseFor use on metal sufaces where a hard, glossy and adherent finish coat is required, specially in home appliances. |
|
Surface PreparationRemove oil grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blating to minimum SA2, preferably to SA2 ½ (for repair and maintenance) Abrasive blasting to Sa 2 ½, SSPC-10 (for new steel) |
|
SARV COAT 3619 |
ACRYLIC clear COATINGS |
|
|
|
|
|
DescriptionSarv coat 3619 is a solvent born clear based on thermoplastic acrylic resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. non pigmented Volume Solids............................... 40±2% Specific Gravity............................ 0.92±0.02 gr/cm3 Flash Point..................................... 33°C Recommended D.F.T................... 30-40 microns Theoretical coverage.................... 13-10 sqm/lit. 14-10.8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 1 hrs.at 20°c Hard dry......................................... 16 hrs.at 20°c Shelflife ......................................... 12 months at 25°c Package.......................................... 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush Nozzle orifice................................. .017”- .019” Nozzle pressure............................. 100 bar/1450 Psi Application temperature............. 5-40°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-36 Pot life ............................................ N/A Recoat interval.............................. Min. 3 hrs. Max. Non limitation |
Outstanding Characteristics
|
|
Recommended UseAs a clear coat on metal, wood gypseous and concrete surfaces onto sealer to make surfaces smooth. |
|
Surface PreparationThe surface must be clean, dry& free from dust.
|
|
SARV COAT 3620 |
ACRYLIC topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 3620 is a quick drying paint based on thermoplastic acrylic resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. Upon request Volume Solids............................... 65±2% Specific Gravity............................ 1.5±0.1gr/cm3 Flash Point..................................... 30°c Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 6.3-9.5 sqm/lit. 8.48-5.56 sqm/kg Heat resistance.............................. 120 °C Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs.at 20°c Hard dry......................................... 14 hrs.at 20°c Shelflife ......................................... 12 months at 25°c Package.......................................... 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush Nozzle orifice................................. .018”- .021” Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-36 Pot life ............................................ N/A Recoat interval.............................. No limitation |
Outstanding Characteristics
|
|
Recommended UseFor use as a finish coat on coating system of steel substrates, where a hard, glossy and adherant finish coat is required. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as dust, grease, oil, salt and loose paint.
|
|
SARV COAT 3621 |
acrylic primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 3621 Is a quick drying primer based on acrylic resin.
|
Physical Data
Finish............................................... Flat Colour............................................. limited Volume Solids............................... 40±2% Specific Gravity............................ 1.30±0.5gr/cm3 Flash Point..................................... 30°c Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10.5-7 sqm/lit. 7.77-5.18 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 60 min at 20°C Hard dry......................................... 16 hrs at 20°C 14 hrs at 35 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air Sprag /Brush, Roller Nozzle oridice................................ .018” - .021” Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-40°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-36 Pot life ............................................ N/A Recoat interval.............................. No limitation
|
Outstanding Characteristics
|
|
Recommended UseFor use on metal sufaces where a hard conating and corrosion protection is required. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3. |
|
SARV COAT 3622 |
ACRYLIC putty COATINGS |
|
|
|
|
|
DescriptionSarv coat 3622 is a quick drying putty based on thermoplastic acrylic resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 60±2% Specific Gravity............................ 2.1±0.05 gr/cm3 Flash Point..................................... 70°C Touch dry....................................... 30 min .at 20°c Hard dry......................................... 24 hrs.at 20°c Shelflife ......................................... 12 months at 20°c Package.......................................... 20 liter container Application DetailsApplication method..................... Knife Application temperature............. 0-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-36 Pot life ............................................ N/A Over coating ................................. Min. 24 hrs. Max. Non limitation |
Outstanding Characteristics
|
|
Recommended UseApplicable for filling pores & smoothing the concrete and wood and carbon steel surfaces. The consistency can be adjusted by thinner SVT- 36 |
|
Surface PreparationThe surface must be clean, dry and free from any contaminations such as grease, rust, salt and loose paint.
|
|
SARV COAT 3929 |
ACRYLIC emulsion sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 3929 is a physically drying penetration primer based on acrylic emulsion resin.
|
Physical Data
Finish............................................... Flat Colour............................................. clear Volume Solids............................... 12±2% Specific Gravity............................ 1.03±0.05 gr/cm3 Recommended D.F.T................... 5-10 microns Theoretical coverage.................... 24-12 sqm/lit. 23.3-11.65 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min. at 20°c 10 min. at 30°C Hard dry......................................... 4 hrs. at 20°C 2 hrs. at 35°C Shelf life ........................................ 12 months Package.......................................... 20 liter container Application DetailsApplication method..................... Air spray, Brush, Roller Nozzle orifice................................. .017”- .021” Nozzle pressure............................. 100 bar/ 1450 Psi Application temperature............. 10-40°c Mixing ratio................................... single pack Thinner/Cleaner............................ water Pot life ............................................ N/A Recoat interval.............................. Min. 4 hrs. Max. Indefinite |
Outstanding Characteristics
|
|
Recommended UseAs a sealer on concrete & masonry substrates for interior and exterior of buildings. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, salt and loose paint.
|
|
SARV COAT 3930 |
ACRYLIC emulstion topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 3930 is a waterborne alkali resistant, acrylic topcoat in ant carbonation system. The product is water- repellent, but allows water vapour from the substrate pass through the film.
|
Physical Data
Finish............................................... Flat Colour............................................. limited Volume Solids............................... 43±2% Specific Gravity............................ 1.45±0.05 gr/cm3 Recommended D.F.T................... 100-150 microns Per two coats Theoretical coverage.................... 4.3-2.86 sqm/lit. 2.96-1.97 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min.at 20°c Hard dry......................................... 5 days at 20°c Shelflife ......................................... 12 months Package.......................................... 20 liter container Application DetailsApplication method..................... Air spray, Brush, Roller Application temperature............. 5-40°c Mixing ratio................................... single pack Thinner/Cleaner............................ water Pot life ............................................ N/A Recoat interval.............................. Min. 6 hrs. Max. None |
Outstanding Characteristics
|
|
Recommended UseAs a topcoat applicable in paint system in interior and exterior of buildings. |
|
Surface PreparationThe surface of primer must be clean, dry and free from any contamination such as grease, salt and loose paints.
|
|
SARV COAT 3931 |
ACRYLIC emulsion primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 3931 is a physically drying primer based on acrylic emulsion resin.
|
Physical Data
Finish............................................... Flat Colour............................................. limited Volume Solids............................... 45±2% Specific Gravity............................ 1.45±0.05 gr/cm3 Recommended D.F.T................... 30-50 microns Theoretical coverage.................... 13.3-8 sqm/lit 9.3-5.6 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min .at 20°c Hard dry......................................... 3 days at 20°c Shelf life ........................................ 12 months Package.......................................... 20 liter container Application DetailsApplication method..................... air spray, Brush, Roller Application temperature............. 10-40°c Mixing ratio................................... single pack Thinner/Cleaner............................ water Pot life ............................................ N/A Recoat interval ............................. Min. 6 hrs. Max. None |
Outstanding Characteristics
Promotes adhesion between coating layers & substrate.
|
|
Recommended UseAs a primer on concrete & masonary interior & exterior of wall and buildings. |
|
Surface PreparationThe surface must be clean, dry& free from any contamination such as grease, salt and loose paint.
|
|
SARV COAT 4968 |
polyester topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 4968 is baking hard topcoat enamel based on modified saturated polyester resin.
|
Physical Data
Finish............................................... Gloss, semi gloss Colour............................................. Upon request Volume Solids............................... 46±2% Specific Gravity............................ 1.1 ±0.01 gr/cm3 D.F.T............................................... 46-60 microns Flash point..................................... 23 °C Theoretical coverage.................... 11.5-9.2 sqm/lit 9.2-7.36 sqm/kg Practical Coverage....................... Depends on loss factor Flash of time ................................. 10-15 min Baking temperature..................... 150-160 °C Baking timer.................................. 25-30 min Shelf life......................................... 1 year
|
Outstanding Characteristics
|
|
Recommended UseFor use on methal surfaces (specially nonferrous metals) where a hard, glossy and adherent finish coat is required, specially in roll coating . |
|
Surface PreparationThe surface must be clean, dry and free from rust, mill scale, salt and loose paint. Sand blasting or wire brushing to a standard of ST 2 (SA.2.5, SIS 05 5900, ISO 8501-1) is repuired. |
|
SARV COAT 6119 |
alkyd baking clear COATINGS |
|
|
|
|
|
DescriptionSarv coat 6119 is a baking glossy clear coat based on a modified alkyd resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. Clear Volume Solids............................... 40±2% Specific Gravity............................ 1±0.05 gr/cm3 Flash Point..................................... 30°C Recommended D.F.T................... 20-40 microns Theoretical coverage.................... 22-11 sqm/lit. 22-11 sqm/kg Practical Coverage....................... Depends on loss factor Flash time....................................... 10 min at 20°C Stoving time................................... 15-20 min at 160°C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller, deep Nozzle orfice.................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Thinner/Cleaner............................ SVT-61 Recoat interval.............................. Wet on wet or after . Partially curing |
Outstanding Characteristics
|
|
Recommended UseFor use on metal surfaces where a hard glossy and adherant finish coat is required, specially in home appliances. |
|
Surface PreparationThe surface must be clean & dry. All dirt, grease, mill scales & any other foreign materials should be removed.
|
|
SARV COAT 6120 |
alkyd baking enamel COATINGS |
|
|
|
|
|
DescriptionSarv coat 6120 is a baking glossy topcoat based on a modified alkyd resin.
|
Physical Data
Finish............................................... Gloss, Semi gloss Colour............................................. Upon request Volume Solids............................... 42±3% Specific Gravity............................ 1.15±0.1 gr/cm3 (black: 10) Flash Point..................................... 26°C Recommended D.F.T................... 25-40 microns Theoretical coverage.................... 16.8-10.5 sqm/lit. 14.6-9.1 sqm/kg Practical Coverage....................... Depends on loss factor Flashing time................................. 10 min Stoving time................................... 15-20 min at 160°C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller, deep Nozzle orfice.................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-61 Pot life ............................................ N/A Recoat interval.............................. Wet on wet or after . Partially curing |
Outstanding Characteristics
|
|
Recommended UseFor use on metal surfaces where a hard glossy and adherant oily finish coat is required, specially in home appliances. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum Sa2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½ SSPC10 -(for new steel)
|
|
SARV COAT 6219 |
alkyd ureaclear(varnish) COATINGS |
|
|
|
|
|
DescriptionSarv coat 6219 is a tow component clear coat based on alkyd urea formaldehyde.
|
Physical Data
Finish............................................... Gloss Colour............................................. no pigmented Volume Solids............................... 58±2% Specific Gravity............................ 1.0±0.05 gr/cm3 Flash Point..................................... 25°C Dry film thickness......................... 40 microns Touch dry....................................... 30 min at 20°C Hard dry ........................................ 48 hrs Theoretical coverage.................... 15 sqm/lit. 15 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 12 months Package.......................................... 4 & 20 liter container Application DetailsApplication method..................... Air Spray Application temperature............. 10-50°c Thinner/Cleaner............................ SVT-62 Mixing ratio................................... 7/1 by weight Pot life ............................................ 8 hours Recoat interval.............................. ---
|
Outstanding Characteristics
|
|
Recommended UseAs a clear topcoat for decorating and protecting wood surfaces. The cured film has good stain resistance against cold and hot drinks as well as washing liquids. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, and any other foreign materials should be removed old primed surfaces must be smoothly brushed by sand paper.
|
|
SARV COAT 6368 |
alkyd fast drying topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 6368 is a versatile finish coat based on fast drying alkyd resin.
|
Physical Data
Finish............................................... Gloss , semi gloss Colour............................................. upon request Volume Solids............................... 45±2% Specific Gravity............................ 2.10±0/5 gr/cm3 Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10-6.6 sqm/lit. 8.7-5.8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... Max. 45 min at 20°C Hard dry......................................... 1 week at 20°C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .018"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ration................................. single pack Thinner/Cleaner............................ SVT-63 Pot life............................................. N/A Recoat interval.............................. Min 15 hrs. Max indefinite |
Outstanding Characteristics
|
|
Recommended UseAs a finish coat over alkyd primed industrial steel surfaces sush as industrial engines, automobiles, wagons, containers etc |
|
Surface PreparationThe surface must be undamaged, clean, dry and free from any contamination such as grease, rust, salt and loose paint.
|
|
SARV COAT 6719 |
alkyd clear COATINGS |
|
|
|
|
|
DescriptionSarv coat 6719 is air-drying alkyd clear.
|
Physical Data
Finish............................................... Gloss Colour............................................. non pigmented Volume Solids............................... 42±2% Specific Gravity............................ 0.9±0.05 gr/cm3 Flash Point..................................... 33°C Dry film thickness......................... 30-35 microns Touch dry....................................... 3 hrs at 20°C Hard dry......................................... 5-7 days at 20°C Theoretical coverage.................... 12-14 sqm/lit 13.30-15.50 sqm/kg Practical coverage........................ depends on loss factor Shelf life ........................................ 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Brush, Roller and Air spray Application temperature............. 10-50°c Thinner/Cleaner............................ SVT-67 Pot life ............................................ N/A Recoat interval.............................. Min. 6 hrs. Max None |
Outstanding Characteristics
|
|
Recommended UseAs a clear coat on metal, wood, gypseous and concrete surfaces onto sealer to make surfaces smooth. |
|
Surface PreparationThe surface must be clean, dry & free from dust.
|
|
SARV COAT 6720 |
alkyd sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 6720 is air-drying alkyd sealer.
|
Physical Data
Finish............................................... semi gloss Colour............................................. non pigmented Volume Solids............................... 40±2% Specific Gravity............................ 1±0.05 gr/cm3 Flash Point..................................... 30°C Dry film thickness......................... 25 microns Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 6 days Theoretical coverage.................... 16.8 sqm/lit. 16 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air Spray, Brush, Roller Application temperature............. 10-50°c Thinner/Cleaner............................ SVT-67 Pot life ............................................ N/A Recoat interval.............................. Min. 1 hrs. Max 2 days |
Outstanding Characteristics
|
|
Recommended UseAs a mist coat on metal and sealer coat on concrete surfaces to penetrate into the pores make porous surfaces smooth. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum Sa2, preferably to Sa2 ½ (for repair and maintenance) Abrasive blasting to Sa 2½, SSPC-10 (for new steel)
|
|
SARV COAT 6721 |
alkyd topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 6721 is a versatile finish coat based on long oil alkyd resin.
|
Physical Data
Finish............................................... semi gloss/ gloss Colour............................................. Upon request Volume Solids............................... 50±2% Specific Gravity............................ 1.15±0.01 gr/cm3 Flash Point..................................... 33°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10.4-6.9 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 3 hrs at 20°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... 120°C Shelf life ........................................ 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .019”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max indefinite |
Outstanding Characteristics
|
|
Recommended UseAs a finish coat on exterior and interior of steel structures, wood substrates and massonaries, previously primed with alkyd primers. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, salt and loose paint. Old primed surfaces should be roughened before repainting.
|
|
SARV COAT 6722 |
alkyd mio interm ediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 6722 is a versatile intermediate/finish coat based on long oil alkyd resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 54±2% Specific Gravity............................ 1.45±0.05 gr/cm3 Flash Point..................................... 38°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13.5-9 sqm/lit. 9.3-6.2 sqm/kg Touch dry....................................... 18 min at 20°C 2 hrs at 35°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... continuous 120°C Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Package.......................................... 4 or 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .019”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT 67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseAs an intermediate/finish coat on exterior and interior of steel structures previoush primed with alkyd primers. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, salt and loose paint. Old primed surfaces should be roughened.
|
|
SARV COAT 6723 |
alkyd intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 6723 is a versatile intermediate coat based on long oil alkyd resin.
|
Physical Data
Finish............................................... semi flat/Semi gloss Colour............................................. Upon request Volume Solids............................... 53±2% Specific Gravity............................ 1.2±0.05 gr/cm3 Flash Point..................................... 33°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12-8 sqm/lit. 9.23-6.15 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 180 min at 20°C Hard dry......................................... 7 week at 20°C Thermal Resistance...................... 120°C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .019”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseAs an intermediate coat on exterior and interior of steel structures, wood substrates and massonaries, previously primed with alkyd primers. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, salt and loose paint. Old primed surfaces should be roughened before over coating.
|
|
SARV COAT 6724 |
alkyd zinc phosphate COATINGS |
|
|
|
|
|
DescriptionSarv coat 6724 is a preventing, zinc phosphate pigmented Primer based on long oil alkyd resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 53±2% Specific Gravity............................ 1.3±0.05 gr/cm3 Flash Point..................................... 33°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12-8 sqm/lit. 8.57-5.71 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 180 min at 20°C Deep dry......................................... 1 week at 20°C Thermal Resistance...................... 120°C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .018”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseFor use on structural steel e.g building, ware houses, bridges, as part of a suitable alkyd based paint system. |
|
Surface PreparationRemove oil and grease, etc with suitable detergent Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3.
|
|
SARV COAT 6725 |
alkyd zinc chromate COATINGS |
|
|
|
|
|
DescriptionSarv coat 6725 is rust preventing, zinc chromate pigmented primer based on oil alkyd resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Yellow, Green Volume Solids............................... 53±2% Specific Gravity............................ 1.33±0.05 gr/cm3 Flash Point..................................... 33°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12.5-8.3 sqm/lit. 9.25-6.17 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 180 min at 20°C Hard dry......................................... 1 week at 20°C Shelf life ........................................ 12 months at 25°C Thermal Resistance...................... 120°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .018”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT 67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseFor use on structural steel e.g buildings, ware houses and bridges, as part of a suitable alkyd based paint system. |
|
Surface PreparationRemove oil and grease, etc with suitable sovent. Remove salt and other contaminants by (high pressure) fresh water cleaning. A brasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3.
|
|
SARV COAT 6726 |
alkyd red oxid rrimer COATINGS |
|
|
|
|
|
DescriptionSarv coat 6726 is a general purpose red oxide primer based on long oil alkyd resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Red-Brown Volume Solids............................... 48±2% Specific Gravity............................ 1.5±0.05 gr/cm3 Flash Point..................................... 38°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12-8 sqm/lit. 8-5.3 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 3 hrs at 20°C Hard dry......................................... 1 weak at 20°C Shelf life ........................................ 12 months at 25°C Thermal Resistance...................... 100°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .018”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT 67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseFor use on structural steel to be topcoated with oil based finish coats. |
|
Surface PreparationRemove oil and grease, etc with suitable detergent Remove salt and other contaminants by (high pressure) fresh water cleaning. A brasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3.
|
|
SARV COAT 6726-9 |
alkyd red oxide zinc oxide primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 6726-9 is a primer based on raw linseed oil and alkyd resin, containing zinc oxide and iron oxide pigments, according to SSPC paint 25 Type II.
|
Physical Data
Finish............................................... Flat-Semi flat Colour............................................. Red Volume Solids............................... 70±1% Specific Gravity............................ 1.5±0.04 gr/cm3 Flash Point..................................... 38°C Recommended D.F.T................... 45-55 microns Theoretical coverage.................... 16-13.1 sqm/lit. 10-8.2 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 20 hrs at 25°C Hard dry......................................... 36 hrs at 25°C Shelf life ........................................ 12 months at 20°C Thermal Resistance...................... 120°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Nozzle orifice................................. .018”- .021” Nozzle pressure............................. 150 bar/ 2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseFor use on interior and exterior of structural steel to be top coated with conventional paint systems. |
|
Surface PreparationRemove oil and grease, etc with suitable solvent. Remove salt and other contaminants by (high pressure) fresh water cleaning. A brasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3.
|
|
SARV COAT 6727 |
alkyd primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 6727 is a general purpose primer based on long oil alkyd resin.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 57±1% Specific Gravity............................ 1.5±0.05 gr/cm3 Flash Point..................................... 38°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13.75-9.16 sqm/lit. 9.82-6.54 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 3 hrs at 20°C Hard dry......................................... 1 week at 20°C Shelf life......................................... 12 months at 25°C Thermal Resistance...................... 120°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush, Roller Nozzle orifice................................. . .018"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 67 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 1 months |
Outstanding Characteristics
|
|
Recommended UseFor use on structural steel to be topcoated with oil based finish coats. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to minimum Sa 2 alternatively power tool cleaning to ST3.
|
|
SARV COAT 6729 |
alkyd PHENOLIC TOPCOAT |
|
|
|
|
|
DescriptionSarv coat 6729 is a one component alkyd finish coat modified with phenolic.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 60±2% Specific Gravity............................ 1.30±0.05 gr/cm3 Flash Point..................................... 23°C Recommended D.F.T................... 50-60 microns Theoretical coverage.................... 12-10 m²/lit. 8-6 m²/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 1 hrs at 25°C Fully cured..................................... 4 days at 25°C Shelf life ........................................ 24 months at 20°C Thermal Resistance...................... Continuous 120°C Non-continuous 130°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 67 Recoat interval.............................. Min. 24 hrs. Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a protection coating in industrial and marine structures over concrete or metal surface. Resistance to a variety of chemicals , fuel oils and solvents. As a general purpose is suitable for lining storage tanks ship tanks exposed to immersion, splash sea mater |
|
Surface PreparationThe surface must be clean and dry . All dirt, grease, mill scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed. Blast to sa 3 ISO 8501 or SSPC 5,the roughness profile should be 40-75 micron. |
|
SARV COAT 6730 |
FAST DRYING alkyd TOPCOAT |
|
|
|
|
|
DescriptionSarv coat 6730 is a gloss fast drying alkyd topcoat.
|
Physical Data
Finish............................................... Gloss Colour............................................. Upon request Volume Solids............................... 48±2% Specific Gravity............................ 1.2±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-50 microns Theoretical coverage.................... 12.5-9.6 sqm/lit. 10-8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 15-20 minutes at 20°C Hard dry......................................... 16 hrs at 20°C Fully cured..................................... 14 hrs at 35°C Shelf life ........................................ 12 months at 20°C Thermal Resistance...................... Continuous 90°C Non-continuous 110°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Application temperature............. 5-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 67 Pot life ............................................ N/A Recoat interval.............................. Min. 24 hrs. Max 1 months |
Outstanding Characteristics
|
|
Recommended UseAs a finish coat to be used over Sarv coat 6725 for protection as a topcoat & decorative purposes. |
|
Surface PreparationThe surface must be clean , dry and free from any Contamination such as grease , dirt , salt and loose paint. Old primed surfaces should be roughened before repainting.
|
|
SARV COAT 6868 |
alkyd hich closstopcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 6868 is a general purpose glossy topcoat based on medium oil alkyd resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. Upon request Volume Solids............................... 50±2% Specific Gravity............................ 1.15±0.1 gr/cm3 Viscosity(Ford cup No.4)............. 180±10 sec Flash Point..................................... 30°C Recommended D.F.T................... 40-60 microns Touch dry....................................... 1.5 hrs at 20°C Hard dry......................................... 16 hrs at 20°C Theoretical coverage.................... 12.5-8.3 sqm/lit. 10.8-7.2 sqm/kg Practical Coverage....................... Depends on loss factor Thermal Resistance...................... continuous 120°C Noncontinuous 130°C Shelf life ........................................ 12 months at 20°C Package.......................................... 20 liter container Application DetailsApplication method..................... Air /Airless spray, Brush, Roller Application temperature............. 5-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-68 Pot life ............................................ N/A Recoat interval.............................. Min. 16 hrs. Max indefinite |
Outstanding Characteristics
|
|
Recommended UseAs a high gloss finish coat over alkyd primed industrial steel surfaces sush as industrial enfines, automobiles, wagons, containers etc... |
|
Surface PreparationThe surface must be undamaged, clean, dry and free from any contamination such as grease, rust salt and loose paint.
|
|
SARV COAT 7168 |
chlorinated rubber swimming pool COATINGS |
|
|
|
|
|
DescriptionSarv coat 7168 is a physically drying, modified chlorinated rubber based coating.
|
Physical Data
Finish............................................... Flat Colour............................................. blue and or request Volume Solids............................... 46±2% Specific Gravity............................ 1.25±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 27-100 microns Theoretical coverage.................... 6.1-4.6 sqm/lit. ......................................................... 4.93-3.70 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 8 hrs at 20°C Shelf life ........................................ 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller. Nozzle orfice.................................. . .021"-.023" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-71 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C Max none (see remarks overleaf) |
Outstanding Characteristics
|
|
Recommended UseAs a water resistant paint in swimming pools or cementitious water reservoirs. |
|
Surface PreparationThe surface must be clean and dry. Remove oil, grease, salt and any other contamination with suitable solvent and by high pressure fresh water.
|
|
SARV COAT 7729 |
chlorinated rubber sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 7729 is a sealer physically drying, modified chlorinated rubber based.
|
Physical Data
Finish............................................... Flat Colour............................................. non pigmented Volume Solids............................... 36±2% Specific Gravity............................ 1.23±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 20-40 microns Theoretical coverage.................... 18-9 sqm/lit. 14.63-7.31 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 15 min at 20°C Hard dry......................................... 24 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller. Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant saler in underwater and above water systems such as ships hulls, decks and superstructures, offshores, structural steel and pipping in chemical plants, refineries, bridges and cranes. |
|
Surface PreparationThe surface must be clean and dry. Remove oil, grease, salt and any other contamination with suitable detergent and by high pressure fresh water.
|
|
SARV COAT 7730 |
chlorinated rubber hich build COATINGS |
|
|
|
|
|
DescriptionSarv coat 7730 is a high build physically drying, modified chlorinated rubber based topcoat.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Upon request Volume Solids............................... 42±2% Specific Gravity............................ 1.25±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 50-80 microns Theoretical coverage.................... 8.4-5.2 sqm/lit. 6.7-4.2 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 2 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller. Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT -77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant coat in underwater and above water systems such as ships hulls, decks and superstructures, offshores, structural steel and pipping in chemical plants, refineries, bridges and cranes. It is also suitable for drinking water systems. |
|
Surface PreparationThe surface must be clean, dry and free of grease, mill- scale, rust and dirt.
|
|
SARV COAT 7731 |
chlorinated rubber top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 7731 is a physically drying, modified chlorinated rubber based topcoat.
|
Physical Data
Finish............................................... Gloss, Semi gloss Colour............................................. Upon request Volume Solids............................... 38±2% Specific Gravity............................ 1.15±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 9.5-6.3 sqm/lit. 8.3-5.5 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 15 min at 20°C Hard dry......................................... 2 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller. Nozzle orifice................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Pai Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant topcoat in underwater and above water systems such as ships hulls, decks and superstructures, offshores, structural steel and pipping in chemical plants, refineries, bridges and cranes. It is also suitable for drinking water systems. |
|
Surface PreparationThe surface must be clean, dry and free of grease, mill- scale, rust and dirt.
|
|
SARV COAT 7732 |
chlorinated rubber MIo interaediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 7732 is a physically drying, plastisized chlorinated rubber based intermediate coat, containing M.I.O as a rust preventing pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 40±2% Specific Gravity............................ 1.25±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10-6.6 sqm/lit. 8-5.3 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 2 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsAir/Airless spray, .......................... Application method Brush, Roller. Nozzle orifice................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant intermediate coat in underwater and above water systems such as ships hulls, decks and superstructures, offshores, structural steel and pipping in chemical plants, refineries, bridges and cranes. It is also suitable for drinking water systems. |
|
Surface PreparationThe surface must be clean, dry and free of grease, mill- scale, rust and dirt.
|
|
SARV COAT 7733 |
chlorinated rubber intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 7733 is a physically drying, modified chlorinated rubber based intermediate.
|
Physical Data
Finish............................................... Flat, Semi gloss Colour............................................. Upon request Volume Solids............................... 40±2% Specific Gravity............................ 1.25±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10-6.6 sqm/lit. ......................................................... 8-5.3 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 24 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Bursh, Roller Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant intermediate in underwater and above water systems such as ships hulls, decks and superstructures, offshores structural steel and pipping in chemical plants, bridges and cranes. It is also suitable for drinking water systems. |
|
Surface PreparationThe surface must be clean, dry and free of grease, mill- scale, rust and dirt.
|
|
SARV COAT 7734 |
chlorinated rubber zinc chromate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 7734 is a physically drying, modified chlorinated rubber based primer, coating Zinc chromate as rust preventing pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. light.yellow Volume Solids............................... 41±1% Specific Gravity............................ 1.3±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 11.2-7.5 sqm/lit. 9-6 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 60 min at 20°C Hard dry......................................... 3 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Bursh, Roller Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a maintenance water resistant primer for use on exterior and interior steel surfaces in moderately to severely corrosive environment. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST2 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel)
|
|
SARV COAT 7735 |
chlorinated rubber red lead primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 7735 is a physically drying, modified rubber based primer.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 40±2% Specific Gravity............................ 1.5±0.05 gr/cm3 Flash Point..................................... 40°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10-6.6 sqm/lit. 7.7-5.1 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 2 hours at 20°C Thermal Resistance...................... Continuous 60°C Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Bursh, Roller Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a maintenance water resistant primer for use on exterior and interior steel surfaces in moderately to severely corrosive environment. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum Sa2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC10 -(for new steel)
|
|
SARV COAT 7736 |
chlorinated rubber red oxide primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 7736 is a physically drying modified chlorinated rubber based primer, containing red oxide as rust preventing pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Red-Brown Volume Solids............................... 45±2% Specific Gravity............................ 1.25±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 11.2-7.5 sqm/lit. 9-6 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 2 hours at 20°C Thermal Resistance...................... Continuous 60°C Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsAir/Airless spray,........................... Application method Brush, Roller Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT- 77 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 25°C
|
Outstanding Characteristics
|
|
Recommended UseAs a water resistant primer in underwater and above water systems such as ships hulls, decks and superstructures, offshores structures, structural steel and pipping in chemical plants, refineries, bridges and cranes. It is also suitable for drinking water systems. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10(for new steel)
|
|
SARV COAT 7737 |
chlorinated rubber TRAFFIC PAINT |
|
|
|
|
|
DescriptionSarv coat 7737 is a physically drying, modified chlorinated rubber based traffic paint.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 40±2% Specific Gravity............................ 1.35±0.05 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 100-150 microns Theoretical coverage.................... 4-2.7 sqm/lit. ......................................................... 2.96-2 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 60 min at 20°C Hard dry......................................... 24 hours at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 12 months at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Automatic or hand application Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-77 Pot life ............................................ N/A Recoat interval.............................. No limitation
|
Outstanding Characteristics
|
|
Recommended UseSuitable for use on concrete and asphalt , specially for road marking. |
|
Surface PreparationThe surface must be clean, dry and free of grease, mill- scale, rust and dirt.
|
|
SARV COAT 7988 |
chlorinated rubber synthetic primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 7988 is a physically quick drying systhetic primer it consist of chlorinated rubber and plasticizer and colouring matter, together with solvents needed to give a consistency suitable for application by spray, brush or other approved method. The technical data meets BS4147 Type "B" requirements.
|
Physical Data
Finish............................................... Gloss Colour............................................. Blak Volume Solids............................... 39±2% Specific Gravity............................ 0.95±0.02 gr/cm3 Flash Point..................................... 24°C Recommended D.F.T................... 30-40 microns Theoretical coverage.................... 9.6-7.5 sqm/lit. 9.47-7.1 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 10 min at 20°C Hard dry......................................... 120 min at 20°C Thermal Resistance...................... Continuous 60° Non-continuous 65 °C Shelf life ........................................ 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush, Roller. Nozzle orfice.................................. . .017"-.021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°c Mixing ratio................................... single pack Thinner/Cleaner............................ SVT -79 Pot life ............................................ N/A Recoat interval.............................. Min 6 hrs at 20°C Max none |
Outstanding Characteristics
|
|
Recommended UseThis synthetic primer for cold and hot application is used with coating materials (usually Hot Bituminous enamel, Hot coal tar enamels and cold wrapping tape) it is quick drying and application of the subsequent coating is possible within a shor time. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST2 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel) |
|
SARV COAT 8150 |
coaltar Epoxy COATINGS |
|
|
|
|
|
DescriptionSarv coat 8150 is a high build two component, corrosion preventing tar-epoxy coating, according to IPS-M-TP-190.
|
Physical Data
Finish............................................... Semi flat – semi gloss Colour............................................. Dark borwn, Black Volume Solids............................... 80±2 Specific Gravity............................ 1.30±0.05 gr/cm3 Flash Point..................................... 26°C Dry film Thicknss......................... 200-400 microns Theoretical Coverage................... 2-4 sqm/lit 1.54-3.08 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... Max. 8 hrs at 20°C Hard dry......................................... Max. 14 days at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . 0.021"-0.023" Nozzle pressure............................. 200 bar/2900 Psi Application temperature............. 10-50°C Mixing ratio................................... 4/ 1 by weight Cleaner........................................... SVT-18 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs at 20°C Max 72 days at 20°C |
Outstanding CharacteristicsSarv coat 8150 coal tar epoxy is suitable for use in cold & hot climates It can easily applied in very thick coat. It is excellent rust preventing. Chemical resistance against hydrochloric acid, sodium hydrochloric, salt water and sour crude oil. |
|
Recommended UseFor protection of steel in marin structures, pilling , crude oil tanks, ships bottom, pipe coating, power plants, petrochemical & oil refining plants. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½ SSPC-10 with a sharp –edged surface profile corresponding to Rugotest No.3, BN9a, Keane- Tator comparator, 2.0 G/S or ISO comparator, medium (G).
|
|
Typical recommended paint system1or2 layers of 100-200 µ each sarv coat 8150 on bare steel 1 layer of epoxy sealer sarv coat 8729-10r2 layers of 100-200 µ each sarv coat 8150 on concrete. |
|
|
SARV COAT 8219 |
Epoxy ester clear COATINGS |
|
|
|
|
|
DescriptionSarv coat 8219 is a single pack clear coat based on epoxyester resin.
|
Physical Data
Finish............................................... Gloss Colour............................................. clear Volume Solids............................... 38±2% Specific Gravity............................ 0.95 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 20-40 microns Theoretical coverage.................... 19-9.5 sqm/lit 20-10 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 20 min at 20°C Hard dry......................................... 40 min at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 12 months 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-82 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 3 months |
Outstanding Characteristics
|
|
Recommended UseAs a clear coat in industrial and marine structures such as refineries, petrochemical plants, bridges, tanks and water sewage plants. |
|
Surface PreparationThe surface must be clean & dry. Any contamination sush as dirt, grease, Oil, salt and any other foreign materials should be removed. |
|
SARV COAT 8220 |
Epoxy esters ealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8220 is a single pack sealer based on epoxy ester resin.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Non- pigmented Volume Solids............................... 42±2% Specific Gravity............................ 1.1 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 20-40 microns Theoretical coverage.................... 20-10 sqm/lit 18.18-9.09 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 30 min at 20°C Hard dry......................................... 48 hrs at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 20°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-82 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs ......................................................... Max 3 months |
Outstanding Characteristics
|
|
Recommended UseAs a sealer in industrial and structures such as refineries, petrochemical plants, bridges, tanks and water sewage plants. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (for repair and maintenance) abrasive blasting to SA 2 ½ SSPC-10 (for new steel) |
|
SARV COAT 8221 |
Epoxy Ester top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 8221 is a single pack topcoat based on epoxy ester resin.
|
Physical Data
Finish............................................... Gloss, Semi gloss Colour............................................. Upon uequest Volume Solids............................... 48±2% Specific Gravity............................ 1. 2 ±0.05 gr/cm3 Flash Point..................................... 23°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12-8 sqm/lit 10 -6.7 sqm/kg Partical Coverage......................... depends on loss factor Touch dry....................................... 2 hrs at 20°C 1 hrs at 35°C Hard dry......................................... 16 hrs at 20°C 12 hrs at 35°C Thermal Resistance...................... continuous 100°C Non- continuous 150°C Shelf life......................................... 1 year Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Application temperature............. 10-50°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-82 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 3 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a topcoat in industrial and marine structures such as refineries, petrochemical plants, bridges, tanks and water sewage plants. |
|
Surface PreparationThe surface must be clean and dry. Any contamination such as dirt, grease, oil, salt and any other foreign materials should be removed. |
|
|
SARV COAT 8222 |
Epoxy Ester intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8222 is a single pack coating based on epoxy ester resin.
|
Physical Data
Finish............................................... semi gloss Colour............................................. Upon uequest Volume Solids............................... 38±2% Specific Gravity............................ 1.33 ±0.05 gr/cm3 Flash Point..................................... 23°C Recommended.............................. 40-60 microns Theoretical coverage.................... 9.5-6.33 sqm/lit 7.14 -4.76 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 60 min at 20°C Hard dry......................................... 20 hrs at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-82 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 3 months |
Outstanding Characteristics
|
|
Recommended UseAs a intermediate or topcact in industrial and marine structures such as refineries, petrochemical plants, bridges, tanks and water sewage plants. |
|
Surface PreparationThe surface must be clean and dry. Any contamination such as dirt, grease, oil, salt and any other foreign materials should be removed. |
|
SARV COAT 8223 |
Epoxy Ester primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8223 is a single pack primer based on epoxy ester resin. Containing corrosi on- resistant pigment.
|
Physical Data
Finish............................................... Creyor other shades Colour............................................. Non- pigmented Volume Solids............................... 43±2% Specific Gravity............................ 1.33 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 10.75-7.16 sqm/lit 8.5-38 sqm/kg Practical coverage ....................... dependsonloss factor. Touch dry....................................... 30 min at 20°C Hard dry......................................... 48 hrs at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 20°C Package.......................................... 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019"-.023" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-82 Pot life ............................................ N/A Recoat interval.............................. Min 24 hrs Max 3 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a prlmer in industrial and marlne structures such as refineries, petrochemical plants, bridges, tanks and water sewage plants. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor aress) Or by abrasive blasting to minimum SA2, Preferably to Sa2 ½ (for repair and maintenance) abrasive blasting to Sa 2 ½ SSPC-10 (for new steel) |
|
SARV COAT 8568 |
polyamine cured Epoxy VinyL topcoat COATINGS |
|
|
|
|
|
DescriptionSarv coat 8568 is a physically drying topcoat based on a vinyl copolymer resin. |
Physical Data
Finish............................................... Gloss, semi gloss Colour............................................. Upon request Volume Solids............................... 41±2% Specific Gravity............................ 1.1 ±0.05 gr/cm3 Flash Point..................................... 25°C Recommended D.F.T................... 30-50 microns Theoretical coverage.................... 13.6-8.2 sqm/lit 12.4-7.45 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT- 85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a versatile topcoat for vinyl systems on exterior steel structures exposed in moderately to severely industrial and marine corrosive environment. |
|
Surface PreparationThe surface must be clean, dry and free from any contamination such as grease, rust, mill scale, salt and loose paint. |
|
SARV COAT 8569 |
hich build Epoxy VinyL intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8569 is a two component, vinyl polyamide cured epoxy intermediate. |
Physical Data
Finish............................................... semi gloss Colour............................................. Upon request Volume Solids............................... 42±2% Specific Gravity............................ 1.1 ±0.05 gr/m3 Flash Point..................................... 26°C Recommended D.F.T................... 50-70 microns Theoretical coverage.................... 8.4-6.0 sqm/lit ......................................................... 7.6-5.45 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a protective intermediate coat in industrial and marine structures, over concrete or metal surfaces. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed. |
|
SARV COAT 8570 |
Epoxy VinyL hich build intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8570 is a two component, polyamide cured epoxy- vinyl intermediate coat. Also suitable suitable as "Tie coat" between epoxy & physically drying coating.
|
Physical Data
Finish............................................... semi gloss Colour............................................. Upon request Volume Solids............................... 53±2% Specific Gravity............................ 1.3 ±0.05 gr/m3 Flash Point..................................... 26°C Recommended D.F.T................... 50-100 microns Theoretical coverage.................... 10.6-5.3 sqm/lit 8.1-4.1 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner..................................... SVT- 85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a protective intermediate coat for industrial and marine structures, over epoxy & zinc ethyl silicate primer. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease & any other foreign matter should be removed. Old primed surfaces must be smoothly wire brushed. |
|
SARV COAT 8571 |
Epoxy VinyL hich bulid primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8571 is a two component, vinyl polyamida cured epoxy primer.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 44±2% Specific Gravity............................ 1.15 ±0.05 gr/cm3 Flash Point..................................... 23°C Recommended D.F.T................... 70-80 microns Theoretical coverage.................... 6.28-5.5 sqm/lit 5.46-4.78 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a protective intermediate coat in industrial and marine structures, over concrete or metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor aress) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (for repair and maintenance) abrasive blasting to SA 2 ½ SSPC-10 (for new steel) |
|
SARV COAT 8572 |
Epoxy VinyL zing dust primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8572 is a two component, polyamide cured epoxy modified by vinyl containing zinc dust.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 58±2% Specific Gravity............................ 1.8 ±0.05 gr/m3 Flash Point..................................... 23°C Recommended D.F.T................... 70-80 microns Theoretical coverage.................... 8.2-7.2 sqm/lit 4.6-4.0 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT- 85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a protective primer coat in industrial and marine structures, over concrete or metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor aress) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (for repair and maintenance) abrasive blasting to SA 2 ½ SSPC-10 (for new steel) |
|
SARV COAT 8573 |
epoxy vinyl zinc phosphte primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8573 is a two component, polyamide cured epoxy vinyl primer, containing zinc phosphate as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Yellow, Grey, Green Volume Solids............................... 53±2% Specific Gravity............................ 1.3±0.05 gr/cm3 Flash Point..................................... 26°C Recommended D.F.T................... 40-60 microns Theoretical Coverage................... 13.3-8.8 sqm/lit 10.2-6.8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hours at 20°C 1 hrs at 35°C Fully cured..................................... 7 days at 20°C 6 days at 35°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 20°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50 °C Mixing ratio................................... 4 /1 by weight Thinner/Cleaner............................ SVT-85 Pot life ............................................ 8 hrs at 20 °C Recoat interval:............................ Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer, for epoxy and urethane systems on steel and other metal surfaces. |
|
Surface PreparationSand blasting or wire brushing to a standard of ST2(SA 2.5, SIS 05 5900, ISO 8501-1) is perquisite. |
|
SARV COAT 8574 |
Epoxy vinyl Primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8574 is a two component, polyamide cured epoxy vinyl primer coat.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 52±2% Specific Gravity............................ 1.35 ±0.05 gr/m3 Flash Point..................................... 26°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13-8.7 sqm/lit 9.62-6.41 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... Max 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life......................................... 1 year at 25°C Package.......................................... 5- 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-85 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 4 months |
Outstanding Characteristics
|
|
Recommended UseAs a protective primer coat for industrial and marine structures. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor aress) Or by abrasive blasting to minimum SA2, Preferably to SA2 ½ (for repair and maintenance) abrasive blasting to SA 2 ½ SSPC-10 (for new steel) |
|
SARV COAT 8729 |
Epoxy polyamide sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8729 is a two component polyamide cured, epoxy sealer. It is possible to formulate with MIO and without MIO.
|
Physical Data
Finish............................................... Semi flat Colour............................................. Red oxide Volume Solids............................... 57±2% Specific Gravity............................ 1.4 ±0.05 gr/m3 Flash Point..................................... 27°C Dry Film Thickness....................... 40-60 microns Touch dry....................................... 2 hrs at 20°C Hard dry(fully cured)................... 1 week at 20°C Thermal Resistance...................... 140 °C Theoretical coverage.................... 14.25-9.5 sqm/lit 10.17-6.78 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life......................................... 12 months at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method, ................... Air/Application spray, Brush Nozzle orifice................................. .019”-.021” Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval:............................ min 6 hrs max none
|
Outstanding Characteristics
|
|
Recommended UseAs sealer coat on metal surfaces and as an intermediate coat on zinc silicates to minimize popping. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damage area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, preferably to SA2½(for repair and maintenance) Abrasive blasting to Sa2½SSPC-10 (for new steel)
|
|
SARV COAT 8729-7 |
Epoxy polyamide sealer/fuller COATINGS |
|
|
|
|
|
DescriptionSarv coat 8729-7 is a two component, polyamide cured epoxy sealer.
|
Physical Data
Finish............................................... Glossy Colour............................................. None Volume Solids............................... 57±2% Specific Gravity............................ 1.2±0.05 gr/cm3 Flash Point..................................... 27°C Dry Film Thickness....................... 20-40 microns Touch dry....................................... 2-4 hrs at 20°C Hard dry (fully cured).................. 7 days at 20°C Thermal Resistance...................... 140°C Theoretical coverage.................... 28.5-14.25 sqm/lit. 23.75-11.87 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless spray, Bursh Nozzle orifice................................. . .017"-.021" Nozzle pressure............................. 100 bar/1450 Psi Application temperature............. 10-50°C Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 6 hrs at 20°C Max none |
Outstanding Characteristics
|
|
Recommended UseAs a sealer coat on metal surfaces, concrete and as a tie coat on ethyl silicate primer. |
|
Surface PreparationThe surface must be clean & dry. All dirt, Grease, mill scales and any other foreign materials should be removed. In the case of flooring the surface shall be scraped by appropriate tools.
|
|
SARV COAT 8729-8 |
Epoxy polyamide sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8729-8 is a two component, polyamide cured epoxy sealer.
|
Physical Data
Finish............................................... Glossg Colour............................................. Transparent Volume Solids............................... 40% Specific Gravity............................ 0.90±0.05 gr/cm3 Flash Point..................................... 24°C Dry Film Thickness....................... 20-40 microns Touch dry....................................... 2-3 hrs at 20°C Hard dry (fully cured).................. 7 days at 20°C Thermal Resistance...................... 140°C Theoretical coverage.................... 22.5-11.25 sqm/lit. 23-11.4 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless spray, Bursh Nozzle orifice................................. . .013"-.017" Nozzle pressure............................. 100 bar/1450 Psi Application temperature............. 10-50°C Mixing ratio................................... 3/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval.............................. Min 6 hrs at 20°C Max none |
Outstanding Characteristics
|
|
Recommended UseAs a sealer coat on concrete, steel substrate & floors subjected electrical conductivity. |
|
Surface PreparationThe surface must be clean and dry. All dirt, Grease, mill scales and any other foreign materials should be removed. In the case of flooring the surface shall be scraped by appropriate tools.
|
|
SARV COAT 8730 |
Epoxy polyamide high build MIO COATINGS |
|
|
|
|
|
DescriptionSarv coat 8730 is a two component polyamide cured, high build epoxy coating, containing micaceous iron oxide.
|
Physical Data
Finish............................................... Semi flat Colour............................................. light grey & Red Volume Solids............................... 58%(ASTM-D-2697 modified) Specific Gravity............................ 1.36 kg/L(white) Flash Point..................................... 24°C Dry Film Thickness....................... 75-125 sqm/lit Touch dry....................................... 1 hrs at 20°C Hard dry......................................... 7 days at 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Theoretical coverage.................... 7.6- 4.5 sqm/lit ......................................................... 5.2- 3.1 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsAir/Airless spray, .......................... Air/Application spray, Brush Nozzle orifice................................. .019”-.021” Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... 4/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseFor protection of structural steel in refineries, mining pulp and paper industries, water sewage plants, bridges, storage tanks and peteochemical plants. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. (For maintenacce) Abrasive blasting to Sa 2½ , SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G). (For new steel)
|
|
SARV COAT 8731 |
Epoxy polyamide high build/high solid self primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8731 is a two component polyamide cured, high build epoxy primer & intermediate, containing zinc phosphate as corrosion inhigiting pigment.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Upon request Volume Solids............................... 85% (ASTM-D-2697 modified) Specific Gravity............................ 1.31 kg(mixed produet) Flash Point..................................... 24°C Dry Film Thickness....................... 125 microns per coat Theoretical coverage.................... 6.8 m2/L at 125 microns Touch dry....................................... 6 hrs at 20°C Hard dry......................................... 7 days 20°C 5 days at 35°C Thermal Resistance...................... 140 °C Practical Resistance..................... depends on loss factor Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. .021” Nozzle pressure............................. 50 bar/3600 Psi Mixing ratio................................... Base/Hardener 4/1/ by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... (24 hrs at 20°C) Recoat interval max:................... (14 days at 20°C) |
Outstanding Characteristics
|
|
Recommended UseAs a high build, rust preventing primer & intermediate for epoxy and urethane systems on steel and other metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½, SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G).
|
|
SARV COAT 8732 |
|
Epoxy polyamide high build COATINGS |
||
|
|
|
|
|
|
DescriptionSarv coat 8732 is a two component polyamide cured, high build epoxy coating, applicable as intermediate & topcoat.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Upon request Volume Solids............................... 65±2% Specific Gravity............................ 1.40±0.05 gr/cm³ Flash Point..................................... 26°C Recommended D.F.T................... 100-125 microns Theoretical coverage.................... 6.5- 5.2 m²/lit 4.6- 3.7 m²/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Fully cured..................................... 1 week at 20°C Thermal Resistance...................... Continuous 110 °C Non-Continuous 130°C Shelf life......................................... 24 month at 20°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .019" - .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. .10-50°C Mixing ratio................................... Refer to the can label Thinner/Cleaner............................ SVT-87 Pot life ............................................ 4 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs
|
|
Outstanding Characteristics
|
||
Recommended UseAs a high build, high performance protective coating in aggressive environment over concrete or metal substrate (interior and exterior surfaces). |
||
Surface PreparationThe surface must be clean and dry.All dirt,grease,mill-scales and any other foreign materials should be removed. Sand blasting or wire brushing to a standard of ST 2 is required.
|
|
SARV COAT 8732-8 |
Epoxy high build multipurpose COATINGS |
|
|
|
|
|
DescriptionSarv coat 8732-8 is a two component polyamide cured, high build Multipurpose epoxy coating.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Upon request Volume Solids............................... 58% (ASTM-D-2699) Specific Gravity............................ 1.50 kg/l Flash Point..................................... 24°C Recommended D.F.T................... 100 microns/ per coat Theoretical coverage.................... 5.8 m2/lat 100 microns Practical Coverage....................... Depends on loss factor Touch dry....................................... 1 hrs at 20°C Fully cured..................................... Seven days 20°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Application DetailsApplication method .................... Air/airless spray, Brush Nozzle orifice................................. .018”-.021” Nozzle pressure............................. 250 bar/3600 Psi Application temperature............. 10-50 °C Mixing ratio................................... 5(A)+1(B) Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a high build, high performance protective coating in aggressive environment over metal substrate of ships brges, Tank & structural steel in chemical plants refineries. Offshore platforms, sea water. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. (For maintenacce) Abrasive blasting to Sa 2½ , SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G). (For new steel)
|
|
SARV COAT 8732-9 |
Epoxy polyamide high solid COATINGS |
|
|
|
|
|
DescriptionSarv coat 8732-9 is a two component polyamide cured, high solid epoxy coating.
|
Physical Data
Finish............................................... Semi gloss-gloss Colour............................................. Upon request Volume Solids............................... 45% (ASTM-D-2699 modifed) Specific Gravity............................ 1.16 kg/l Flash Point..................................... 24°C Recommended D.F.T................... 100-150 microns Theoretical coverage.................... 6.5-4.33 sqm/lit 4.64-3.09 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 1 hrs at 20°C 2 hrs at 35 °C Fully cured..................................... 7 days 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Package.......................................... 4&20 liter container Application DetailsAir/Airless method, ...................... Air/Application spray, Brush Nozzle orifice................................. .018”-.021” Nozzle pressure............................. 250 bar/3600 Psi Mixing ratio................................... Base/Hardener 5/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a high solid, high performance protective coating in aggressive environment over concrete or metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. (For maintenacce) Abrasive blasting to Sa 2½, SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G). (For new steel)
|
|
SARV COAT 8733 |
Epoxy polyamide top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 8733 is a two component, polyamide cured epoxy topcoat.
|
Physical Data
Finish............................................... Gloss-Semi gloss Colour............................................. Upon request Volume Solids............................... 52%(ASTM-D-2697) Specific Gravity............................ 1.33 kg/L Flash Point..................................... Not applicable packaging Recommended D.F.T................... 50 microns Theoretical coverage.................... 10.4 m2/lit Practical Coverage....................... Depends on loss factor Touch dry....................................... 180 min 20°C 2 hrs at 35°C Fully cured..................................... 7 days at 20°C 1 week at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Application spray, Brush Nozzle orifice................................. . .021” Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base / Hardener 4/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a protective topcoat in industrial and marine structures, over concrete or metal surfaces. |
|
Surface PreparationThe surface must be clean and dry, All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed.
|
|
SARV COAT 8734 |
Epoxy polyamide mio intermdiate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8734 is a two component, polyamide cured epoxy coating, containing micaceous iron oxide.
|
Physical Data
Finish............................................... Flat- semi Flat Colour............................................. light grey& Red Volume Solids............................... 53% Specific Gravity............................ 1.40 Flash Point..................................... 30°C Recommended D.F.T................... 50-75 sqm/lit Theoretical coverage.................... 7.6-5 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C 1 hrs at 35°C Fully cured..................................... Seven days at 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. .019”-.021” Nozzle pressure............................. 175 bar/2200 Psi Mixing ratio................................... Base/Hardener 4/1/ by weight Thinner/Cleaner............................ SVT- 87 Pot life ............................................ 8 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseFor protection of structural steel in refineries, mining pulp and paper industries, water sewage plants, bridges, storage tanks and petrochemical plants. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. (For maintenacce) Abrasive blasting to Sa 2½, SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G). (For new steel)
|
|
SARV COAT 8735 |
Epoxy polyamide intermdiate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8735 is a two component, polyamide cured epoxy intermediate coat.
|
Physical Data
Finish............................................... Semi Flat Colour............................................. Upon request Volume Solids............................... 63% Specific Gravity............................ 1.40 kg/L Flash Point..................................... 30°C Recommended D.F.T................... 125 microns Theoretical coverage.................... 5.0 m2/L at 125 microns Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Fully cured..................................... 7 days at 20°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. ..021” Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base / Hardener 4/1 by weight Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a protective intermediate coat in industrial and marine structures, over concrete or metal surfaces. |
|
Surface PreparationThe surface must be clean and dry, All dirt, grease, mill- scales and other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed.
|
|
SARV COAT 8736 |
|
3 pack zinc rich Epoxy primer COATINGS |
||
|
|
|
|
|
|
DescriptionSarv coat 8736 is a three component, polyamide cured epoxy primer, containing zinc dust (third component) as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 63±2 % Solid by weight.............................. 90±2% Zinc content in dry film............... ~91±1% by weight Specific Gravity............................ 3.1±0.1 gr./cm3 Flash Point..................................... 26°C Recommended D.F.T................... 50-75 microns Theoretical coverage.................... 12.6-8.4 m2/L. 4.06-2.70 m2/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 45 min at 20°C 25 min at 35°C Hard dry......................................... 1 week at 20°C 6 days at 35°C Thermal Resistance...................... Continuous 180°C Non-continuous 200°C Shelf life......................................... 12 months at 20 °C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray Brush Nozzle orifice................................. . .019" - .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. .5-50° C Mixing ratio................................... Refer to the can label Thinner/Cleaner SVT- 87 Pot life ............................................ 8 hrs at 20°C Recoat interval:............................ Min 24 hrs Max 72 hrs
|
|
Outstanding Characteristics
|
||
Recommended UseAs a versatile long- life primer on steel, suitable for application on industrial structures to be exposed in severe corrosive atmospheres. |
||
Surface PreparationSand blasting or wire brushing a standard of ST 2 (SA 2.5,SIS 05 5900,ISO 8501-1)
|
|
SARV COAT 8736-7 |
|
2 pack zinc rich Epoxy primer COATINGS |
||
|
|
|
|
|
|
DescriptionSarv coat 8736-7 is a two component, polyamide cured epoxy pimer, containing zinc dust as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey Volume Solids............................... 63±2% Solid by weight ............................. 90±2 Zinc content in dry film............... ~91±1% by weight Specific Gravity............................ 3±0.1 gr./cm3 Flash Point..................................... 26°C Recommended D.F.T................... 50-75 microns Theoretical coverage.................... 12.6-8.4 m2/Lit 4.2-2.8 m2/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 1-2 hrs at 20°C Hard dray……………………….1 week at 20°C Thermal Resistance...................... Continuous 180 °C Non- Continuous 200 °C Shelf life......................................... 12 months at 20°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Application spray, Brush Nozzle orifice................................. . .019" - .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Mixing ratio................................... Refer to the can label Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs Recoat interval max:................... 72 hrs |
|
Outstanding Characteristics
|
||
Recommended UseAs a versatile long- life primer on steel, suitable for application on industrial structures to be exposed in severe corrosive atmospheres. |
||
Surface PreparationSand blasting or wire brushing a standard of ST 2 (SA 2.5,SIS 05 5900,ISO 8501-1).
|
|
SARV COAT 8736-8 |
2 pack zing rich Epoxy primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8736-8 is a two component, polyamide cured epoxy pimer, containing zinc dust as corrosion inhibiting pigment. The qualiy meets SSSC Panint 20, 1nd class of zinc rich coating.
|
Physical Data
Finish............................................... Flat Colour............................................. Grey, Red grey Volume Solids............................... 45% (ASTM-D-2697) Specific Gravity............................ 2.15 kg/lit Flash Point..................................... 30°C Recommended D.F.T................... 65 microns Theoretical coverage.................... 6.9 m 2 /l Practical Coverage....................... Depends on loss factor Touch dry....................................... 2-3 hrs at 20°C 1 hrs at 35°C Fully cured..................................... Seven days 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Application DetailsApplication method , .................. Air/Application spray, Brush Nozzle orifice................................. .017”-.021” Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... A/B/ 19/1 by weight Thinner/Cleaner............................ SVT- 87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a versatile long- life primer on steel, suitable for application on industrial structures to be exposed in medium corrosive atmospheres. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Abrasive blasting to Sa 2½ , SSPC-10 with a sharp-edged surface profile corresponding to rugotest No.3, BN9a, keane – Tator comparator, 2.0 G/S or ISO comparator, medium(G).
|
|
SARV COAT 8736-9 |
ZINcA |
|
|
|
|
|
DescriptionSarv coat 8736-9 one component zinc copmpound , ready for use with brush , based on aromatic hydrocarbons. ZINCA corresponds to the European standards ISO 3549 – 1987 and DIN 55 969 (zinc concentration in the dry extract of 96 %) and to ISO 752 and DIN 1706 (zinc purity of 99, 995 %)
|
Physical Data
Specific gravity............................. 2.75 ± 0.05 Kg / dm³ Dry extract..................................... 82 % (weight) or 39.8 % (volume) Zinc content in dry extract.......... minimum 95% - 98% (weight) Temperature resistance............... 200 º C (400ºF) +150 / - 40 Viscosity at delivery..................... 3000 to 4600 cps (Brookfield RVT / Spindle # 5 / 100 RPM 20 º C) or DIN / FORD Cup n º 4 : ± 60 sec. Flash point..................................... 47 º C
Recommended D.F.T................... 100 – 200 microns
Theoretical coverage.................... 1.41 – 0.70 sqm/kg
Recommended D.F.T................... 65 microns
Colour............................................. metallic grey ( colour changes on contact with humidity ) Packaging....................................... (1,2,5,10 and 25 Kg) (1,5,25 and 200 Lit) Touch dry....................................... 10 min at 15°C
Head resistance............................. +150 / 040
Application DetailsApplication method , .................. Air/Application spray, Brush Thinner/Cleaner............................ SVT- 87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C |
Physical dataZINCA can be applied using most conventional application methods such as brush , roller , airspray – gun and airless spray. Other application methods using aerosols or by dipping are possible. |
|
|
|
Surface conditionThe best cathodic protection with ZINCA will be obtained when blasting to a standard Sa 2.5 with a roughness Rz of approx. 50 µm. (ISO 8501-1 : 1998). In some cases a hand cleaning to a standard St 2 can be sufficient. All surfaces must be prepared to the ISO 8501 -1standard . Application temperature must be above 5 º C and the difference between surface temperature and dew point greater than 3 º C . For specific recommendations .contact your Zingametall representative. |
|
SARV COAT 8737 |
Epoxy polyamide zing phosphate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8737 is a tow component, polyamide cured epoxy primer, containing zinc phoshphate as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Yellow, Grey, Green Volume Solids............................... 55% (ASTM-D-2697 modifid) Specific Gravity............................ 1.33 kg/L Flash Point..................................... 25°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13.3-8.8 sqm/lit. 10.2-6.8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 3 hrs at 20°C 2 hrs at 35°C Fully cured..................................... seven days at 20 °C 6 doys at 35 °C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 20°C Package.......................................... 5 & 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush Nozzle orifice................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base/Hardener 4/1 by weight Thinner/Cleaner............................ SVT 87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20 °C |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer for epoxy and urethane systems on steel and other metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel).
|
|
SARV COAT 8738 |
Epoxy polyamide zinc chromate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8738 is a two component polyamide cured epoxy primer containing zinc chromate as corrosion inhibiting pigment .
|
Physical Data
Finish............................................... Flat Colour............................................. light yellow, green Volume Solids............................... 53% Specific Gravity............................ 1.3±0.05 gr/cm3 Flash Point..................................... 26°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13.3-8.8 sqm/lit. 10.2-6.8 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 3 hrs at 20°C 2 hrs at 35°C Fully cured..................................... seven days at 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base/Hardener 4/1 by weight Thinner/Cleaner............................ SVT- 87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20 °C |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer for epoxy and urethane systems on steel and other metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel).
|
|
SARV COAT 8739 |
Epoxy polyamide red oxide primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8739 is a two component polyamide cured epoxy primer containing red oxide as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat Colour............................................. Red Volume Solids............................... 51%±2 Specific Gravity............................ 1.35±0.05 gr/cm3 Flash Point..................................... 26°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12.8-8.5 sqm/lit. 9.5-6.3 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C 6 days at 35°C Fully cured..................................... seven days at 20°C 6 days at 35°C Thermal Resistance...................... 140 °C Shelf life......................................... 1 year at 20°C Package.......................................... 5 & 20 liter container Application DetailsApplication method..................... Air/Airless spray, Brush Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... single pack Thinner/Cleaner............................ SVT-87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20 °C |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer for epoxy systems, on steel and other metal surfaces, even primed with sarv coat 1983. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2 (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel).
|
|
SARV COAT 8740 |
Epoxy polyamide primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8740 is a two component polyamide cured epoxy primer or tie coat.
|
Physical Data
Finish............................................... Flat Colour............................................. upon request Volume Solids............................... 51%(ASTM-D-2697 modified) Specific Gravity............................ 1.30±0.05 gr/cm3 Flash Point..................................... 30°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 12.75-8.5 sqm/lit. 9.44-6.3 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 35°C 3 hrs at 20°C Fully dry......................................... seven days at 20°C 6 days at 35°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Application method Brush, Roller. Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base/Hardener 4/1 by weight Thinner/Cleaner............................ SVT- 87 Pot life ............................................ 8 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 14 days at 20° C |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer for epoxy systems, on structural steel, galvanized surfaces, pipes, tanks oil refineries, power plants. Chemical process plants, for immersion and non immersion service, applicable both as primer & tie coat over zinc ethyl silicate. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas) Or by abrasive blasting to minimum SA2, Preferably to Sa2½ (for repair and maintenance) Abrasive blasting to Sa 2½SSPC-10 (for new steel).
|
|
SARV COAT 8819 |
Epoxy polyamine solvent free clear COATINGS |
|
|
|
|
|
DescriptionSarv coat 8819 is a two component, polyamine cured, solvent free transparent epoxy coat.
|
Physical Data
Finish............................................... Gloss Colour............................................. Transparent Volume Solids............................... 100% Specific Gravity............................ 1.11±0.02 gr/cm3 Flash Point..................................... 100°C Recommended D.F.T................... 100-200 microns Theoretical Coverage................... 10-5 sqm/lit 9-4.5 sqm/kg Practical Coverage....................... depends on loss factor Touch dry....................................... 8 hrs at 20°C 5 hrs at 35°C Hard dry......................................... 1 week at 35°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year Application DetailsApplication method .................... Air/Airless Spray Brush, Roller Nozzle orifice................................. .017"- .021" Nozzle pressure............................. 100 bar/1450 Psi Application temperature............. 10-50°C Mixing ratio................................... Base/Hardener/2/1 by weight Cleaner........................................... SVT-88 Pot life ............................................ 30 min at 20°C Recoat interval.............................. Min 16 hrs at 20°C Max 72 hrs at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a transparent epoxy topcoat on epoxy paint systems where a high glossy finish is required or for topcoating of epoxy systems for coating potable water tanks. |
|
Surface PreparationThe surface must be clean & dry All dirt, grease, mill-scales and any other foreign materials should be removed.
|
|
SARV COAT 8820 |
Epoxy polyamine solvent free sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8820 is a two component, polyamine cured, solvent free epoxy primer& sealer with good penetration properties.
|
Physical Data
Finish............................................... Glossy Colour............................................. Transparent Volume Solids............................... 99±1% Specific Gravity............................ 1.45±0.05 gr/cm3 Flash Point..................................... 65°C Dry Film Thickness....................... Depending on surface porosity Touch dry....................................... 4 hrs at 20°C 5 hrs 35°C Hard dry......................................... 1 week at 20°C 5 days at 35°C Thermal Resistance...................... 140°C Theoretical Coverage................... depends on D.F.T Practical Coverage....................... depends on loss factor Shelf life ........................................ 1 year Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Air/Airless spray Brush, Roller Nozzle orifice................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Base/Hardener Mixing ratio................................... 4/1 by weight Thimer/ Cleaner............................ SVT-88 Pot life ............................................ 40 min at 20°C Recoat interval.............................. Min 16 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a sealer for pretreatment of concrete floors, prior to application of epoxy flooring & as a primer in epoxy coating systems. |
|
Surface PreparationThe surface must be clean & dry All dirt, grease, mill-scales and any other foreign materials should be removed. The concrete substrate should be old at least 28 days. The maximum moisture content is 0.6%
|
|
SARV COAT 8821 |
Epoxy polyamine flooring COATINGS |
|
|
|
|
|
DescriptionSarv coat 8821 is a two component, polyamine cured, solvent free epoxy coating.
|
Physical Data
Finish............................................... Gloss Colour............................................. limited Volume Solids............................... 95±2% Specific Gravity............................ 1.45±0.05 gr/cm3 Flash Point..................................... 32°C Dry Film Thickness....................... 1000-3000 microns Theoretical Coverage................... 0.95- 0.31 sqm/lit 0.65-021 sqm/kg Touch dry....................................... 8 hrs at 20°C Hard dry......................................... 48 hrs at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25 °C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Putty Knife, Trowel Application temperature............. 10-50°C Mixing ratio................................... 5/ 1 by weight Pot life ............................................ 60 min at 20°C Recoat interval.............................. Min 8 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a suitable floor coating on concrete or steel industrial floors subjected to continuous mechanical wear and where chemical and solvents resistance is required. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill-scales and any other foreign materials should be removed. Mechanical characteristics(For3 mm film thickness) Compressive strength (BS6319 pt3) 50 N/mm2 Flexural strength (BS6319 pt7) 34 N/mm2 Foot traffic at 20°C 24 hrs Vehicle traffic at 20°C 48 hrs
|
|
SARV COAT 8821-7 |
Epoxy polyamine anti-acid floor COATINGS |
|
|
|
|
|
DescriptionSarv coat 8821-7 is a two component, polyamine cured, solvent free epoxy Anti-Acid floor coating.
|
Physical Data
Finish............................................... Gloss Colour............................................. limited Volume Solids............................... 94±2% Specific Gravity............................ 1.48±0.05 gr/cm3 Flash Point..................................... 32°C Dry Film Thickness....................... 1000-3000 microns Theoretical Coverage................... 0.94- 0.31 sqm/lit 0.63-0.20 sqm/kg Touch dry....................................... 8 hrs at 20°C Hard dry......................................... 48 hrs at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Putty Knife, Trowel Application temperature............. 10-50°C Mixing ratio................................... 6/ 1 by weight Pot life ............................................ 60 min at 20°C Recoat interval.............................. Min 8 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a suitable floor coating on concrete or steel industrial floors subjected to continuous mechanical wear and where, acid, chemical solvents resistance is required. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill-scales and any other foreign materials should be removed. Mechanical characteristics(For3 mm film thickness) Compressive strength (BS6319 pt3) 50 N/mm2 Flexural strength (BS6319 pt7) 34 N/mm2 Foot traffic at 20°C 24 hrs Vehicle traffic at 20°C 48 hrs
|
|
SARV COAT 8821-8 |
Epoxy polyamine anti-staic flooring COATINGS |
|
|
|
|
|
DescriptionSarv coat 8821-8 is a two component, polyamine cured, solvent free epoxy Anti-static floor coating.
|
Physical Data
Finish............................................... Gloss Colour............................................. Grey Volume Solids............................... 97±2% Specific Gravity............................ 1.35±0.05 gr/cm3 Flash Point..................................... 23°C Dry Film Thickness....................... 3000-5000 microns Theoretical Coverage................... 0.19- 0.32 sqm/lit 0.14-0.23 sqm/kg Touch dry....................................... 8 hrs at 20°C The electrical resistance…...........10-1000(ohm) Hard dry......................................... 2 days at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Package.......................................... 5& 20 liter container Application DetailsApplication method .................... Putty Knife, Trowel Application temperature............. 10-50°C Mixing ratio................................... Base /Hardener 4/ 1 by weight Pot life ............................................ 60 min at 20°C Recoat interval.............................. Min 8 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a suitable floor coating on concrete or steel industrial floors subjected to continuous mechanical wear and where electric conductivity and chemical & solvents resistance is required. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill-scales and any other foreign materials should be removed. Mechanical characteristics(For3 mm film thickness) Compressive strength (BS6319 pt3) 50 N/mm2 Flexural strength (BS6319 pt7) 34 N/mm2 Foot traffic at 20°C 24 hrs Vehicle traffic at 20°C 48 hrs E lectric conductivity 106 ohm/cm
|
|
SARV COAT 8822-7 |
Epoxy Fiberclass COATINGS |
|
|
|
|
|
DescriptionSarv coat 8822-7 is a tow component, polyamine cured, solvent free transparent epoxy. The epoxy fiberglass coating for the tank bottom consists of the sarv coat 8822-7 epoxy coating with one or two layers of the chopped strand glassmat plus one layer of the surfacing tissue.
|
Physical Data
Finish............................................... Gloss Colour............................................. Clear Substrate........................................ steel or steel primed with sarv coat 8820 Volume Solids............................... 100 % Specific Gravity............................ 1.1±0.02 gr/cm3 Flash Point..................................... 65°C Recommended D.F.T................... 2.5 mm Theoretical coverage Epoxy............................................. 2.5 litre/sqm Fiberglass mat............................... 450 gram/sqm Fiberglass tissues........................... 30 gram/ sqm Practical Coverage....................... Depends on loss factor Silica sand particle size................ 0.1-0.3 mm Curring time (at 20° C) To recoat........................................ up to 2 days Initial set......................................... 24 hrs Full chemical resistance............... 9 days Thermal Resistance...................... immersed :95°C Non-immersed: 120 °C Shelf life ........................................ 1 year package ......................................... 4 liter container Application DetailsApplication method .................... spray or Roller Base/Hardener Mixing ratio................................... 2/ 1 by weight Cleaner........................................... SVT- 88 Pot life(20°C) .............................. 1.5 hrs for 10 litre
|
Outstanding CharacteristicsSarv coat 8822-7 epoxy laminate system will provide corrosion and chemical resistance to bottoms of water or oil storage tanks, which have suffered from internal corrosion. Sarv coat 8840-7 is specifically resistant to the corrosive environment of crude oil/ water mixtures. It provides great strength and excellent chemical resistance. |
|
Typical UseSarv coat 8822-7 Epoxy laminate system is specifically designed for the lining and/or repair of tank walls and tank bottoms of oil or water storage tanks which are corroded and pitted. |
|
Theoretical Consumptin per m2Sarv coat 8820 primer (tie coat) 0.14 litre Sarv coat 8822-7 filler (surfacer /filler) 380 grams Sarv coat 8822-7 epoxy for sufacer/filler 0.16 litre Sarv coat 8822-7 lining 2.5 litre
|
|
SARV COAT 8823 |
Epoxy polyamine solvent free COATINGS |
|
|
|
|
|
DescriptionSarv coat 8823 is a two component, polyamine cured, solvent free epoxy coating.
|
Physical Data
Finish............................................... Gloss, Semi glass Colour............................................. upon request Volume Solids............................... %100 Specific Gravity............................ 1.45 kg/L Flash Point..................................... 60°C Touch dry....................................... 24 hrs at 20°C Hard dry......................................... 1 week at 20°C Recommended DFT..................... 150-500 mic Thermal Resistance...................... 140°C Theoretical Coverage................... 250 g/m2 500 g/m2 Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Package.......................................... 4&20 liter container Application DetailsApplication method .................... Airless spray Nozzle orifice................................. . .019"-.031" Nozzle pressure............................. 250 bar/3600 Psi Application temperature............. 5-50°C Mixing ratio................................... Base/Hardener 5/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 1 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a solvent free epoxy coating with excellent chemical & mechanical properties, suitable for coating chemical products containers and industrial or marine structures. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning.(For maintenance) Abrasive blasting to Sa 2½ SSPC-10 with a sharp –edged surface profile corresponding to Rugotest No.3, BN9a, Keane- Tator comparator, 2.0 G/S or ISO comparator, medium (G). (For new steel)
|
|
SARV COAT 8824 |
Epoxy polyamine glass flake COATINGS |
|
|
|
|
|
DescriptionSarv coat 8824 is a two component, polyamine cured, high build glass flake epoxy coating.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. limited Volume Solids............................... 68 ± 2 % Weight solied ................................ 80 ± 2 Specific Gravity............................ 1.3±0.05 gr/cm3 (Mixed) Flash Point (closed cup)............... 32°C Touch dry....................................... 10 hrs at 20°C Hard dry......................................... 1 week at 20°C Dry film thickness......................... 300 micnons Theoretical coverage.................... 2.36 sqm/lit 1.74 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Airless 1:60 (See Remark over leaf) Nozzle orifice................................. . .035"-.045" reversible Nozzle pressure............................. 250 bar/3600 Psi Mixing ratio................................... Base/Hardener 6/ 1 by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 1 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a epoxy coating with excellent chemical & mechanical properties, suitable for coating chemical products containers and industrial or marine structures. It protects both steel and concrete structures in severe environments including marine structures petroleum and heavy industrial facilities. |
|
Surface PreparationRemove and oil, grease and other, other contaminants by detergent and salt high pressure fresh water hosing prior to water hosing prior to abrasive blasting. Abrasive blasting to Sa2½ ( ISO 8501-1:1988) with a surface propfile equivalent to regotes No. 3 BN 10b, Keane- tator comprator 3.0 G/S ISO comprator, rough Medium. (G)
|
|
SARV COAT 8824-6 |
epoxy polyamine glass flake COATINGS |
|
|
|
|
|
DescriptionSarv coat 8824-6 is a two component, polyamine cured, solvent free glass flake epoxy coating.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. limited Volume Solids............................... 91 %(ASDM-D 2697) modified Specific Gravity............................ 1.5 kg /L Flash Point(closed cud)................ 30°C Touch dry....................................... 6 hrs at 20°C Hard dry......................................... 1 week at 20°C Dry film thickness......................... 200-750 microns Thermal coverage......................... 4.2 m2/L at 200 microns 1.2 m2/L at 750 microns Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Airless 1:63 (see Remark over leaf) Nozzle orifice................................. 0.035"-0.050" Nozzle pressure............................. 250 bar/3600 Psi Mixing ratio................................... Base/ Hardener 4/1 by weight Thinner/Cleaner............................ SVT 88 Pot life ............................................ 1 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a epoxy coating with excellent chemical & mechanical properties, suitable for coating chemical products containers and industrial or marine structures. It protects both steel and concrete structures in severe environments including marine structures petroleum and heavy industrial facilities. |
|
Surface PreparationRemove any oil, grease and other contaminants by detergent and salt high pressure fresh water hosing prior to abrasive blasting. Abrasive blasting to Sa2 ½(ISO 8501-1:1988) with a surface equivalent to regotest No.3 BN 10b, Keane-tator comprator 3.0 G/S ISO comprator rough Medium.(G)
|
|
SARV COAT 8824-7 |
Epoxy polyamine high build abrasion resistant COATINGS |
|
|
|
|
|
DescriptionSarv coat 8824-7 is a two component, polyamine cured, high build epoxy coating silicium oxide as reinforcing ingredient.
|
Physical Data
Finish............................................... Flat Colour............................................. Upon request Volume Solids............................... 85 %(ASDM-D 2697) Specific Gravity............................ 1.31 kg/L Flash Point..................................... 30°C Reconnended D.F.T ................... 150 microns /percoat Thermal coverage......................... 6.8 m2/L Practical Coverage....................... Depends on loss factor Touch dry....................................... 6 hrs at 20°C Hard dry......................................... 7 days at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless Spray Bursh Nozzle orifice................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 5-50°C Thinner/Cleaner............................ SVT-88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a high build, high performance protective coating in aggressive environment over concrete or metal surfaces where a non skid & abrasion resistant surface is needed. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed.
|
|
SARV COAT 8824 -9 |
Epoxy polyamine glass flake COATINGS |
|
|
|
|
|
DescriptionSarv coat 8824-9 is a two component, polyamine cured, high build glass flake epoxy coating.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. limited Volume Solids............................... 87 % (ASDM-D-2697) modified Specific Gravity............................ 1.3-1.5 kg/L Flash Point (closed cup)............... 36°C Touch dry....................................... 6 hrs at 20°C Hard dry......................................... 1 week at 20°C Dry film tickness........................... 125 microns m2 perecat Theoretical coverage.................... 7 m2/L at 125 microns Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Airless 1:63 (See Remark over leaf) Nozzle orifice................................. . .035"-.050" Nozzle pressure............................. 250 bar/3600 Psi Mixing ratio................................... Base/Hardener 5/ 1 by weight Thinner/Cleaner............................ SVT-88(Max. ro 15%( Pot life ............................................ 1 hrs at 20°C
|
Outstanding Characteristics
|
|
Recommended UseAs a epoxy coating with excellent chemical & mechanical properties, suitable for coating chemical products containers and industrial or marine structures. It protects both steel and concrete structures in severe environments including marine structures petroleum and heavy industrial facilities. |
|
Surface PreparationRemove and oil, grease and other, contaminants by detergent and salt high pressure fresh water hosing prior to abrasive blasting. Abrasive blasting to Sa2½ ( ISO 8501-1:1988) with asurface proflle equivalent to regotest No. 3 BN 10b, Keane- tator comprator 3.0 G/S ISO comprator, rough Medium. (G)
|
|
SARV COAT 8825 |
Epoxy polyamine high build COATINGS |
|
|
|
|
|
DescriptionSarv coat 8825 is a two component, polyamine cured, high build epoxy coating.
|
Physical Data
Finish............................................... Semi gloss Colour............................................. Upon request Volume Solids............................... 69 % (ASTM-D-2697 modified) Specific Gravity............................ 1.73 kg/L Flash Point..................................... 28°C Recommended D.F.T................... 100-150 microns Theoretical coverage.................... 4.6 m2/L at 100 microns 6.9 m2/L at 150 microns Practical Coverage....................... Depends on loss factor Touch dry....................................... 5 hrs at 20°C Fully cured..................................... 1 week at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless spray, Bursh Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... Base/Hardener 10/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a high build, high performance protective coating in aggressive environment over concrete or metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning(For maintenance). Abrasive blasting to Sa2 ½, SSPC-10 with a sharp-edged surface profile corresponding to Rugotest No. 3, BN9a, keane-Tator comparator, 2.0 G/S or ISO comparator medium(G). (For new steel)
|
|
SARV COAT 8826 |
Epoxy polyamine top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 8826 is a two component, amine adduct cured, epoxy topcoat.
|
Physical Data
Finish............................................... Gloss Colour............................................. Upon request Volume Solids............................... 54 % Specific Gravity............................ 1.3±0.05 gr/cm3 Flash Point..................................... 23°C Reconnended D.F.T ................... 50-70 microns Thermal coverage......................... 10.8-7.7 sqm/lit 8.3-5.9 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless Spray Bursh, Roller Nozzle orifice................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... Base / hardener/10/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs an epoxy topcoat with excellent chemical and mechanical properties, suitable for coating chemical products containers. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed.
|
|
SARV COAT 8827 |
Epoxy polyamine intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8827 is a two component, polyamine cured epoxy intermediate coat.
|
Physical Data
Finish............................................... Flat-Semi Gloss Colour............................................. Upon request Volume Solids............................... 57 % Specific Gravity............................ 1.35±0.05 gr/cm3 Flash Point..................................... 23°C Reconnended D.F.T ................... 50-70 microns Thermal coverage......................... 11.4-8.1 sqm/lit 8.4-6 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless Spray Bursh, Roller Nozzle orifice................................. .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... Base / hardener/10/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs an intermediate epoxy coating with excellent chemical and mechanical products containers. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed.
|
|
SARV COAT 8828-8 |
Epoxy polyamine anti-static primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8828-8 is a two component, polyamine cured epoxy anti static primer.
|
Physical Data
Finish............................................... Semi Gloss Colour............................................. Black Volume Solids............................... 65 % Specific Gravity............................ 1.20±0.05 gr/cm3 Flash Point..................................... 30°C Dry Film Thickness ..................... 40-60 microns Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... 140°C Thermal coverage......................... 17.25-11.5 sqm/lit ......................................................... 13.8-9.25 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Bursh, Trowel Application temperature............. 10-50°C Mixing ratio................................... Base / hardener/5/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 90 min at 20°C Recoat interval.............................. Min 24 at 20°C Max 72 hrs at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a primer coat on concrete, floors subjected to electrical conductivity. |
|
Surface PreparationThe surface must be clean & dry. All dirt, Grease, mill scales and any other foreign materials should be removed.
|
|
SARV COAT 8829 |
Epoxy polyamine zing phosphate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8829 is a two component, polyamine cured epoxy primer, containing zinc phosphate as corrosion inhibiting pigment.
|
Physical Data
Finish............................................... Flat- Semi flat Colour............................................. Grey, white Volume Solids............................... 54% Specific Gravity............................ 1.30±0.05 gr/cm3 Flash Point..................................... 26°C Dry Film Thickness....................... 40-60 microns Theoretical coverage.................... 13.5-9 sqm/lit. 10.34-6.9 sqm/kg Touch dry....................................... 2 hrs at 20°C Hard dry......................................... 7 days at 20°C Thermal Resistance...................... 140°C Practical Coverage....................... depends on loss factor Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless spray, Bursh Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... Base/Hardener 10/ 1by weight Thinner/Cleaner............................ SVT- 88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a general purpose rust preventing primer for epoxy and urethane systems on steel and other metal surfaces. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3(minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2½ (for repair and maintenance) Abrasive blasting to Sa 2½ SSPC-10 (for new steel)
|
|
SARV COAT 8829-7 |
surface tolerant Epoxy mastics COATINGS |
|
|
|
|
|
DescriptionSurface tolerant zinc phosphate epoxy mastic is a high solids, high build, fast drying, polyamine epoxy designed to protect steel and concrete in industrial exposures, ideal for maintenance painting and fabrication shop applications. The high solids content ensures adequate protection of sharp edges, corners, and welds.
|
Physical Data
Finish............................................... Gloss Colour............................................. Grey, Red oxide Volume Solids............................... 80 % Weigh solid..................................... 90% ± 2% mixed Specific Gravity............................ 1.45±0.05 gr/cm3 Flash Point..................................... 30°C Recommended D.F.T................... 100-200 microns Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 25°C Through dry................................... 4.30 hours at 25°C Hard dry......................................... 1 week at 25°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Package.......................................... 20/4 liter conatainer Application DetailsApplication method .................... Air/Airless spray, Bursh Application temperature............. 5-50°C Mixing ratio................................... 5 base / 1 hardener Thinner/Cleaner............................ SVT-88 Pot life ............................................ 1.0 hours Recoat interval.............................. Min 2 hours at 20°C Max 72 hrs at 20°C |
Outstanding Characteristics
|
|
Recommended UseFor use over prepared steel and concrete in industrial exposures such as:
|
|
Surface PreparationThe surface must be clean. Dry and free of grease, mill scales and dirt. This product can be applied directly to marginally prepared steel surfaces.
|
|
SARV COAT 8830 |
Epoxy polyamine zinc chromate primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8830 is a two component, polyamine cured epoxy primer, containing zinc chromate as corrosion inhibiting pipment.
|
Physical Data
Finish............................................... Flat- Semi flat Colour............................................. light yellw, Green Volume Solids............................... 54% Specific Gravity............................ 1.35±0.05 gr/cm3 Flash Point..................................... 26°C Recommended D.F.T................... 40-60 microns Theoretical coverage.................... 13.5-9 sqm/lit. 10-67 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C Fully cured..................................... 1 week at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year at 25°C Application DetailsApplication method .................... Air/Airless spray, Bursh Nozzle orifice................................. . .021" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10-50°C Mixing ratio................................... Base/Hardener 10/ 1by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 2 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a highly rust preventing primer for epoxy and urethane systems on steel and other metal surfaces in highly corrosive industrial & marine atmospheres. |
|
Surface PreparationRemove oil and grease, etc. with suitable detergent. Remove salt and other contaminants by(high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3(minor areas) Or by abrasive blasting to minimum SA2, Preferably to SA2½ (for repair and maintenance) Abrasive blasting to Sa 2½ SSPC-10 (for new steel)
|
|
SARV COAT 8831 |
Epoxy polyamine putty COATINGS |
|
|
|
|
|
DescriptionSarv coat 8831 is a two component, polyamine cured, solvent free epoxy putty.
|
Physical Data
Colour............................................. upon request Volume Solids............................... 99±1% Specific Gravity............................ 1.85±0.05 gr/cm3 Flash Point..................................... 65°C Touch dry....................................... 5 hrs at 20°C Hard dry......................................... 1 week at 20°C Thermal Resistance...................... 140°C Shelf life ........................................ 1 year Package.......................................... 20& 20 liter container Application DetailsApplication method .................... knife Application temperature............. 5-50°C Mixing ratio................................... 1/1 by weight Thinner/Cleaner............................ SVT-88 Pot life ............................................ 1 hrs at 20°C Recoat interval.............................. Min 24 hrs Max 72 hrs |
Outstanding Characteristics
|
|
Recommended UseAs a solvent free epoxy coating with excellent chemical & mechanical properties, suitable for coating chemical products containers and industrial or marine structures. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, millscales and any other foreign materials should be removed.
|
|
SARV COAT 8968 |
Epoxy phenolic top coat COATINGS |
|
|
|
|
|
DescriptionSarv coat 8968 is a two component, polyamine cured epoxy phenolic.
|
Physical Data
Finish............................................... Glossy Colour............................................. Upon request Volume Solids............................... 65±2% Specific Gravity............................ 1.4±0.05 gr/cm3 Flash Point..................................... 26°C Recommended D.F.T................... 100-150 microns Theoretical Coverage................... 6.5-4.3 sqm/lit 4.6-3.07 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 4 hrs at 20°C Hard dry......................................... 7 days at 20°C 6 days at 35°C Thermal Resistance...................... Continuous 160°C Non-continuous 180°C Shelf life ....................................... 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .018"-.021" Nozzle pressure............................. 200 bar/2900 Psi Pump ratio..................................... Min 54:1 Mixing ratio................................... Base/Hardener 4/ 1by weight Thinner/Cleaner............................ SVT-89 Pot life ............................................ 2 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 21 days at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a protective coating in industrial and marine structures, Over concrete or metal surfaces. Resistant to a variety of chemicals, fuel oils & solvents. As a general purpose is suitable for lining storage tanks ship tanks exposed to immersion, splash sea water. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must be smoothly wire brushed.
|
|
SARV COAT 8969 |
Epoxy phenolic intermediate COATINGS |
|
|
|
|
|
DescriptionSarv coat 8969 is a two component, high performance modified epoxy coating.
|
Physical Data
Finish............................................... Semi Flat Colour............................................. White, Grey Volume Solids............................... 58±2% Specific Gravity............................ 1.4±0.05 gr/cm3 Flash Point..................................... 26°C Dry film Thicknss......................... 100-150 microns Touch dry....................................... 4 hrs at 20°C Hard dry......................................... 7 days at 20°C 6 days at 35°C Thermal Resistance...................... Continuous 160°C Non-continuos 180 °C Theoretical Coverage................... 5.8-3.8 sqm/lit 4.14-2.75 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .018"-.021" Nozzle pressure............................. 200 bar/2900 Psi Mixing ratio................................... Base/Hardener 4/ 1by weight Thinner/Cleaner............................ SVT-89 Pot life ............................................ 2 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 21 days at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a protective coating in tanks lining or steel structures to be immersed or exposed to splash or spillage of sea or potable water, solvents and chemicals. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. Old primed surfaces must surfaces must be roughenend.
|
|
SARV COAT 8970 |
Epoxy phenolic primer COATINGS |
|
|
|
|
|
DescriptionSarv coat 8970 is a two component, polyamine cured, epoxy phenolic.
|
Physical Data
Finish............................................... Flat Colour............................................. White, Grey, Aluminum Volume Solids............................... 60±2% Specific Gravity............................ 1.4±0.05 gr/cm3 Flash Point..................................... 26°C Dry film Thicknss......................... 50-70 microns Touch dry....................................... 3 hrs at 20°C Hard dry......................................... 7 days at 20°C 6 days at 35°C Thermal Resistance...................... Continuous 160°C Non-continuous 180°C Theoretical Coverage................... 12-8.6 sqm/lit ......................................................... 8.6-6.12 sqm/kg Practical Coverage....................... Depends on loss factor Shelf life ........................................ 1 year at 25°C Package.......................................... 5 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .018"-.021" Nozzle pressure............................. 200 bar/2900 Psi Pump ratio..................................... Min 45:1 Mixing ratio................................... Base/Hardener 4/ 1by weight Thinner/Cleaner............................ SVT-89 Pot life ............................................ 2 hrs at 20°C Recoat interval min:.................... 24 hrs at 20°C Recoat interval max:................... 21 days at 20°C |
Outstanding Characteristics
|
|
Recommended UseAs a protective coating in tanks lining or steel structures to be immersed or exposed to splash or spillage of sea or potable water, solvents and chemicals. |
|
Surface PreparationRemove salt and other contaminants by (high pressure) fresh water cleaning.(For maintenance) Abrasive blasting to Sa 2½ SSPC-10 with a sharp –edged surface profile corresponding to Rugotest No.3, BN9a, Keane- Tator comparator, 2.0 G/S or ISO comparator, medium (G). (For new steel)
|
|
SARV COAT 9519 |
polyurethane varnish COATINGS |
|
|
|
|
|
DescriptionSarv coat 9519 a two component, aliphatic isocyanate cured polyurethane varnish.
|
Physical Data
Finish............................................... Gloss, mate Colour............................................. Non-Pingmented Volume Solids............................... 48±2% Specific Gravity............................ 1.1 ±0.1 gr/Cm3 Flash Point..................................... 30°C Recommended D.F.T................... 30-50 microns Theoretical Coverage................... 16-9.6 sqm/lit 14.5-8.7 sqm/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 5 hrs at 20°C 3 hrs at 35°C Fully Cured.................................... 1 week at 20°C 5 days at 35°C Thermal Resistance...................... 120°C Shelf life......................................... 1 year at 25°C Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017"-.019" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. 10 to 50°C Mixing ratio................................... as recommended on paint label Thinner/Cleaner............................ SVT-95 Pot life ............................................ 5 hrs at 20 °C Recoat interval min:.................... 16 hrs at 20 °C Recoat interval max:................... None with itself |
Outstanding Characteristics
|
|
Recommended UseFor use on polyurethane, epoxy paint system or bare metal where a hard and glossy clear coat is required. |
|
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and other foreign materials should be removed. |
|
SARV COAT 9520 |
polyurethane sealer COATINGS |
|
|
|
|
|
DescriptionSarv coat 9520 is a two component, isosyanate cured aliphatic polyurethane sealer.
|
Physical Data
Finish............................................... Flat Colour............................................. Non pigmented Volume Solids............................... 40±2% Specific Gravity............................ 1.0 ±0.02 gr/m3 Flash Point..................................... 30°C Dry Film Thickness....................... 20-30 microns Touch dry....................................... 5 hrs at 20°C 3hrs at 35°C Fully cured..................................... 1 week at 20°C 5 days at 35°C Thermal Resistance...................... 120°C Shelf life......................................... 1 year at 25°C Package.......................................... 4& 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017"-.019" Nozzle pressure............................. 150 bar/2200 Psi Mixing ratio................................... Base/Hardener 5/1 by weight Thinner/Cleaner............................ SVT- 95 Pot life ............................................ 5 hrs at 20°C Recoat interval min:.................... 16 hrs at 20°C *Recoat interval max:................. none withitself |
Outstanding Characteristics
|
|
Recommended UseFor use on concrete, metal surfaces and as an intermediate coat on zinc silicates to minimize popping. |
|
Surface PreparationSand blasting or wire brushing to a standard of ST2(SA 2.5, SIS 05 5900 ISO 8501-1).For concrete and previously primed surfaces with sarv coat 1983, the surface must be clean and dry. All dirt, grease, mill-scales and any other foreign material should be removed. |
|
SARV COAT 9521 |
|
polyurethane top coat COATINGS |
||
|
|
|
|
|
|
DescriptionSarv coat 9521 a two component, aliphatic isocyante cured polyurethane topcoat.
|
Physical Data
Finish............................................... Gloss/Semi gloss Colour............................................. upon request Volume Solids............................... 50±3% Specific Gravity............................ 1.15 ±0.1 gr/m3 Flash Point..................................... 30°C Recommended D.F.T................... 40-60 microns Theoretical Coverage................... 12.5-8.3 m²/lit 10.8-7.2 m²/kg Practical Coverage....................... Depends on loss factor Touch dry....................................... 2 hrs at 20°C 1.5 hrs at 35°C Fully Cured.................................... 5 days at 20°C 4 days at 35°C Thermal Resistance...................... Continuous 90°C Non-continuous 100°C Shelf life......................................... 12 months Package.......................................... 4 & 20 liter container Application DetailsApplication method .................... Air/Airless spray, Brush Nozzle orifice................................. . .017" Nozzle pressure............................. 150 bar/2200 Psi Application temperature............. . .5 to 50 °C Mixing ratio................................... Refer to the can label Thinner/Cleaner............................ SVT-95 Pot life ............................................ 4 hrs at 20 °C Recoat interval.............................. Min 16 hrs Max 72 hrs |
|
Outstanding Characteristics
|
||
Recommended UseAs a protective finish coat for protection of structural steel where superior performance, attractive appearance, gloss retention and high corrosion resistance is required, shuch as chemical plants, pulp & paper mills, off-shore platforms, petroleum refineries and containers. |
||
Surface PreparationThe surface must be clean and dry. All dirt, grease, mill- scales and any other foreign materials should be removed. For old primed surfaces, it may be necessary to roughen the surface.
|