SARV COAT 1862-7

 coloured acrylic silicone COATINGS

Description

Sarv coat 1862-7 is a temperature resistant, paint, based on modified silicone-acrylic resin.

Physical Data

Finish............................................... Semi Gloss

Colour............................................. limited

Volume Solids............................... 41±2%

Specific Gravity............................ 1.05±0.05 gr/cm³

Flash Point..................................... 25°C

Recommended D.F.T................... 25-40 microns

Theoretical Coverage................... 16.4-10.2 sqm/lit

                                                          15.6-9.7 sqm/kg

Practical Coverage....................... Depends on loss factor

Touch dry....................................... 2 hours at 20°C

Hard dry......................................... after thermal curing

Thermal Resistance...................... Continuous 250°C

Shelf life......................................... 1 year at 25°C

Package.......................................... 20 liter container

Application Details

Application method .................... Air/Airless spray, Brush

Nozzle orifice................................. . .017"

Nozzle pressure............................. 125 bar/1800 Psi

Mixing ratio................................... Single pack

Thinner/Cleaner............................ SVT-18

Pot life ............................................ N/A

Recoat interval min:.................... 24 hrs at 20 °C

Recoat interval max:................... (see Remarks overleaf)

Outstanding Characteristics

• Rust preventing
• Excellent sprayability.
• Excellent recoatability without stoving between coats
• Applicable over zine silicate sarv caot 1983 or directly on blasted steel.

Recommended Use

As a temperature resistant paint, for use in protection of steel surfaces subjected to temperatures up to 250°C.

Surface Preparation

Remove oil and grease, etc. with suitable detergent.

Remove salt and other contaminants by(high pressure) fresh water cleaning.

Abrasive blasting to Sa2½, SSPC-10.