SARV COAT 3568

ACRYLIC baking enamel COATINGS

Description

Sarv coat 3568 is baking glossy topcoat based on thermoset acrylic resin.

Physical Data

Finish............................................... Gloss

Colour............................................. Upon rquest

Volume Solids............................... 36±3%

Specific Gravity............................ 1.15±0.1gr/cm³ Depends on coloul

Flash Point..................................... 23°c

Dry film thickness......................... 25-40 microns

Theoretical coverage.................... 14.4-9 sqm/lit.

                                                          12.5-7.8 sqm/kg

Practical Coverage....................... Depends on loss factor

Flashing time................................. 10 min

Stoving conditions........................ 15-20 min at 150-170°c

Shelflife ......................................... 12 months at 25°c

Package.......................................... 20 liter container

Application Details

Application method..................... Air/Brush, Roller, deep

Nozzle oridice................................ 021”

Nozzle pressure............................. 150 bar/2200 Psi

Application temperature............. 5-50°c

Mixing ratio................................... single pack

Thinner/Cleaner............................ SVT-35

Pot life ............................................ N/A

Recoat interval.............................. wet on wet or after partially curing

Outstanding Characteristics

• High gloss and colour retention
• Good resistance to different environmental conditions
• Excellent sprayability
• High adhesion to different metallic sufaces
• Excellent flexibility

Recommended Use

For use on metal sufaces where a hard, glossy and adherent finish coat is required, specially in home appliances.

Surface Preparation

Remove oil grease, etc. with suitable detergent. Remove salt and other contaminants by (high pressure) fresh water cleaning. Clean damaged area thoroughly by power tool cleaning to ST3 (minor areas)

Or by abrasive blating to minimum SA2, preferably to SA2 ½ (for repair and maintenance) Abrasive blasting to Sa 2 ½, SSPC-10 (for new steel)